Intergranular corrosion resistance of nanostructured austenitic stainless steel

Corrosion resistance of austenitic stainless steel in sulphuric acid

The resistance and susceptibility of austenitic stainless steel, Type 304, exposed to strong tetraoxosulphate (VI) acids (2 and 5 M concentrations) contaminated with sodium chloride at ambient temperatures was investigated by gravimetric and metallographic/scanning electron microscopy surface characterization methods. Scanning electron microscope (SEM) was used to examine and characterize the t...

Low Temperature Thermochemical Treatments of Austenitic Stainless Steel Without Impairing Its Corrosion Resistance

Improvement in the Corrosion Resistance of Austenitic Stainless Steel 316L by Ion Implantation*

In the present work, austenitic stainless steel 316L (SS316L) samples were implanted with Ni and Ni-Cr. A nickel-rich layer about 100 nm in thickness and a Ni-Cr enriched layer about 60 nm thick are formed on the surface of SS316L. The effects of ion implantation on the corrosion performance of SS316L are investigated in a 0.5 M H2SO4 with 2 ppm HF solution at 80°C by open circuit potential (OC...

Alumina nanostructured coating for corrosion protection of 316L stainless steel

Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...

Alumina nanostructured coating for corrosion protection of 316L stainless steel

Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...