Internal Oxidation Behavior of Ag-Ga Alloys

Rapid solidification behavior of Zn-rich Zn–Ag peritectic alloys

Rapid solidification experiments, including laser remelting, melt-spinning and wedge casting, were carried out to investigate the rapid solidification behavior of Zn-rich Zn–Ag peritectic alloys containing up to 9.0 at% Ag. For comparison, Bridgman solidification experiments of the same alloys were also carried out for growth velocities ranging from 0.02 to 4.82 mm/s, which were lower than that...

High Temperature Erosion- Oxidation Behavior of Nickel- Based Alloys Containing Mo in Fluidized Bed Waste Incineration

High-temperature erosion-oxidation behavior of nickel-based alloys containing 0-7 wt.% Mo in fluidized bed waste incineration conditions was studied. A stream of hot condensed air with a flow rate of 25 L/min caused hot silica sand (700 °C) mixed with 0.5 wt.% of chloride salts to hit the specimens for 250 h. By removing the erosive factor, the high-temperature oxidation behavior of the alloys ...

Antibacterial biodegradable Mg-Ag alloys.

The use of magnesium alloys as degradable metals for biomedical applications is a topic of ongoing research and the demand for multifunctional materials is increasing. Hence, binary Mg-Ag alloys were designed as implant materials to combine the favourable properties of magnesium with the well-known antibacterial property of silver. In this study, three Mg-Ag alloys, Mg2Ag, Mg4Ag and Mg6Ag that ...

Dominant recombination centers in Ga(In)NAs alloys: Ga interstitials

Machinability of experimental Ti-Ag alloys.

This study investigated the machinability of experimental Ti-Ag alloys (5, 10, 20, and 30 mass% Ag) as a new dental titanium alloy candidate for CAD/CAM use. The alloys were slotted with a vertical milling machine and carbide square end mills under two cutting conditions. Machinability was evaluated through cutting force using a three-component force transducer fixed on the table of the milling...