Internal Oxidation Thermodynamics and Isothermal Oxidation Behavior of AgSnO2 Electrical Contact Materials
نویسندگان
چکیده
منابع مشابه
Isothermal and cyclic oxidation behavior of AISI 430 ferritic stainless steel coated with titanium
In order to improve the oxidation resistance of ferritic stainless steel, it is possible to deposit a protective coating on steel substrate. In this research through the usage of pack cementation method a coating of titanium was applied on the surface of AISI 430 stainless steel. Scanning Electron-Microscopy (SEM), Energy- Dispersive X-ray spectrometry (EDAX) and X-ray diffraction (XRD) were us...
متن کاملAir Plasma Sprayed Bond Coat Oxidation Behavior and its Resistance to Isothermal and Thermal Shock Loading
An experimental investigation was conducted to find the effect of spraying method of coating of Thermal Barrier Coatings (TBCs) on their oxidation behaviour and resistance to various thermal loading. Isothermal and thermal shock tests were performed in order to study oxidation behaviour of air plasma sprayed Bond Coat (BC) and assess its effect on TBCs lifetime under the stated loadings. Specim...
متن کاملIsothermal and cyclic oxidation of TiAl composites
Titanium Aluminide and TiAl matrix composites reinforced with alumina fibers (PRD166) were fabricated by powder metallurgy. During isothermal oxidation at 950 and 1070 OC, composites containing PRD166 fibers exhibited larger weight gains than monolithic TiAI; the composites showed evidence of oxidation along the perimeter of the fibers. A fiber reaction, which was observed after oxidation in ai...
متن کاملIsothermal Oxidation of Ti2SC in Air
The oxidation behavior of fully dense Ti2SC was studied thermogravimetrically in air in the 500–800°C temperature range. The oxidation product was a single-layer of rutile in all cases. At 800°C, the oxide layer was not protective and the oxidation kinetics were rapid. At 600 and 700°C, and up to ~50 h, the kinetics were parabolic before they became linear. It was only at 500°C that the weight ...
متن کاملOxidation behavior and electrical Characteristics of used interconnects in solid oxide fuel cells at presence of Mn3O4 and MnFe2O4 coatings
In order to enhance the performance of interconnects which are used in solid oxide fuel cells (SOFCs), a protective/conductive coating can be applied. In this research AISI 430 ferritic stainless steel was coated in a Mn-base pack mixture by pack cementation method. In order to evaluate the oxidation behavior, isothermal oxidation was accomplished for 200 h at 800 ºC. Electrical behavior was al...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Rare Metal Materials and Engineering
سال: 2014
ISSN: 1875-5372
DOI: 10.1016/s1875-5372(14)60086-2