Intrinsic coupling of near-tip matrix crack formation to mode III delamination advance in laminated polymeric matrix composites
نویسندگان
چکیده
منابع مشابه
Finite Element Modeling of Delamination Crack Propagation in Laminated Composites
Finite element analysis of the delamination crack propagation in laminated composites is presented. Fracture mechanics based Virtual Crack Closure Technique (VCCT), and the cohesive element technique, have been used to simulate the delamination initiation and propagation under Mode-I type loading. Detailed description of the parameter selection process for these two techniques with ABAQUS®/Stan...
متن کاملMode I Failure of Laminated Polymeric Composites
A mechanical model for the prediction of mode I delamination failure of a laminated double cantilever beam (DCB) type specimen is presented. The volume of material ahead of the crack tip that experiences high stresses due to the presence of the crack tip was replaced by a nonlinear elastic spring foundation. The volume undergoing global deformation due to the external loading was replaced by a ...
متن کاملAn Experimental Study of Dynamic Delamination of Thick Fiber Reinforced Polymeric Matrix Composites
-Dynamic delamination of thick fiber reinforced polymeric matrix composite laminates is investigated using optical techniques and high-speed photography. The laminates used in this work are graphite/epoxy fiber reinforced, 65 percent fiber volume fraction, composite plates consisting of 48 plies (6 mm plate thickness). Two different laminate layups are tested: a quasi-isotropic arrangement and ...
متن کاملCharacterization of the Edge Crack Torsion (ECT) Test for Mode III Fracture Toughness Measurement of Laminated Composites
The edge crack torsion (ECT) test is designed to initiate mode III delamination growth in composite laminates. An ECT specimen is a rectangular laminate, containing an edge delamination at the laminate mid-plane. Torsion load is applied to the specimens, resulting in relative transverse shear sliding of the delaminated faces. The test data reduction schemes are intended to yield initiation valu...
متن کاملNear Quadratic Matrix Multiplication Modulo Composites
We show how one can use non-prime-power, composite moduli for computing representations of the product of two n × n matrices using only n multiplications and additions.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Solids and Structures
سال: 2014
ISSN: 0020-7683
DOI: 10.1016/j.ijsolstr.2014.03.007