Investigation of wear resistance for variable configurations of woven glass-fiber reinforced composite materials
نویسندگان
چکیده
منابع مشابه
Woven Glass Fiber-Reinforced
ment methods and two spec/imen diameters. Flexural strength and modulus of woven glass fiber-reinforced specimens werc significanLly greater than those without woven glass fiber (p<O.OD, Likewise, comprossive strength of reinforced specimens was signifieantly greater than those without woven glass fiber (p<O.Ol), except for specimens rcjnforced with woven glass fiber oriented at a tilt directio...
متن کاملMachinability of glass fiber reinforced plastic (GFRP) composite materials
This paper deals with the study of machinability of GFRP composite tubes of different fiber orientation angle vary from 30 to 90. Machining studies were carried out on an all geared lathe using three different cutting tools: namely Carbide (K-20), Cubic Boron Nitride (CBN) and Poly-Crystalline Diamond (PCD). Experiments were conducted based on the established Taguchi’s Design of Experiments (DO...
متن کاملExperimental Investigation of Behavior of Glass Fiber Reinforced Concrete (GFRC)
The paper presents the results of casting and testing of 264 GFRC specimens. The glass fibers were 25 mm long, with the aspect ratio (L/D) ranging between 1250 and 3570. The parameters studied were the ratio (by weight) of fibers to cement, i.e. F/C=0%, 1.5%, 3%, and 4.5%, and the ratio of coarse to fine aggregates (gravel to sand), i.e. G/S=1.1, 0.7 and 0.2. In total, 12 mix designs were selec...
متن کاملExperimental Investigation of Behavior of Glass Fiber Reinforced Concrete (GFRC)
The paper presents the results of casting and testing of 264 GFRC specimens. The glass fibers were 25 mm long, with the aspect ratio (L/D) ranging between 1250 and 3570. The parameters studied were the ratio (by weight) of fibers to cement, i.e. F/C=0%, 1.5%, 3%, and 4.5%, and the ratio of coarse to fine aggregates (gravel to sand), i.e. G/S=1.1, 0.7 and 0.2. In total, 12 mix designs were selec...
متن کاملMechanical properties of woven glass fiber-reinforced composites.
The aim of this investigation was to measure the flexural and compressive strengths and the corresponding moduli of cylindrical composite specimens reinforced with woven glass fiber. Test specimens were made by light-curing urethane dimethacrylate oligomer with woven glass fiber of 0.18-mm standard thickness. Tests were conducted using four reinforcement methods and two specimen diameters. Flex...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Research Express
سال: 2020
ISSN: 2053-1591
DOI: 10.1088/2053-1591/abb2cf