Isothermal decomposition kinetics of nickel (II) hydroxide powder
نویسندگان
چکیده
منابع مشابه
Effect of CO2 Partial Pressure on the Thermal Decomposition Kinetics of Zinc Carbonate Hydroxide (TECHNICAL NOTE)
In this work, the effect of carbon dioxide partial pressure on the calcination kinetics of high purity zinc carbonate hydroxide has been studied. Non-isothermal analysis has been performed on samples at different CO2 partial pressures by TGA and DTA. It has been found that the calcination behaviour of this material corresponds to the shrinking core model and the reaction mechanism is phase boun...
متن کاملNickel Oxide (NiO) nanoparticles prepared by solid-state thermal decomposition of Nickel (II) schiff base precursor
In this paper, plate-like NiO nanoparticles were prepared by one-pot solid-state thermal decomposition of nickel (II) Schiff base complex as new precursor. First, the nickel (II) Schiff base precursor was prepared by solid-state grinding using nickel (II) nitrate hexahydrate, Ni(NO3)2∙6H2O, and the Schiff base ligand N,N′-bis-(salicylidene) benzene-1,4-diamine) for 30 min without using any solv...
متن کاملThermal behavior and decomposition kinetics of rifampicin polymorphs under isothermal and non-isothermal conditions
The thermal behavior of two polymorphic forms of rifampicin was studied by DSC and TG/DTG. The thermoanalytical results clearly showed the differences between the two crystalline forms. Polymorph I was the most thermally stable form, the DSC curve showed no fusion for this species and the thermal decomposition process occurred around 245 °C. The DSC curve of polymorph II showed two consecutive ...
متن کاملLeaching Kinetics of Stibnite in Sodium Hydroxide
Spherical pellets of antimony sulphide were dissolved in 1 molar sodium hydroxide solutions at different temperatures. It was found that the shrinking core with ash layer model could satisfactorily explain the dissolution process. Using this model it was found that initially the rate controlling step is a chemical reaction with activation energy of 10.2 kJ/mol. As the ash layer builds up, diffu...
متن کاملDISORDER IN LAYERED HYDROXIDES: DIFFaX SIMULATION OF THE X-RAY POWDER DIFFRACTION PATTERNS OF NICKEL HYDROXIDE
Layered metal hydroxides exhibit non-uniform broadening of lines in their X-ray powder diffraction (XRPD) patterns, which cannot always be explained on the basis of crystallite size effects. In the case of hexagonal solids such as nickel hydroxide, DIFFaX simulations of the XRPD patterns show that: (1) stacking faults and turbostratic disorder at low (<30%) incidence selectively broaden the h0l...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Alloys and Compounds
سال: 2015
ISSN: 0925-8388
DOI: 10.1016/j.jallcom.2015.03.256