Lattice softening in nanometer-size iron particles
نویسندگان
چکیده
منابع مشابه
Imaging and magnetometry of switching in nanometer-scale iron particles
The reversal mechanisms in arrays of nanometer-scale ~,40 nm diameter! iron particles are studied by low-temperature Hall magnetometry and room-temperature magnetic force microscopy. Rotation of the net array magnetization at low temperatures ~20 K! occurs by both reversible and irreversible modes, the latter revealed by Barkhausen jumps. Spatially resolved measurements at room temperature show...
متن کاملComparative Cytotoxicity of Nanometer-Size Chromium Oxide and Alumina Particles on Macrophages In Vitro
INTRODUCTION: Joint implant wear particles are recognized to play a major role in initiating periprosthetic osteolysis leading to aseptic loosening and implant failure. It has been shown that particle composition, size, shape and concentration influence the inflammatory response to wear particles [1,2]. Metal-metal (MM) and ceramic-ceramic (CC) bearings are common alternatives to conventional m...
متن کاملNanometer Sized Silver Particles Embedded Silica Particles—Spray Method
Spherical shaped, nanometer to micro meter sized silica particles were prepared in a homogeneous nature by spray technique. Silver nanoparticles were produced over the surface of the silica grains in a harmonized manner. The size of silver and silica particles was effectively controlled by the precursors and catalysts. The electrostatic repulsion among the silica spheres and the electro static ...
متن کاملLattice Softening in Fe3Pt Exhibiting Three Types of Martensitic Transformations
We have investigated the relation between the softening of elastic constants and martensitic transformation in Fe3Pt, which exhibits various kinds of martensitic transformation depending on its long-range order parameter S. The martensite phases of the examined alloys are BCT (S = 0.57), FCT1 (S = 0.75, c/a < 1) and FCT2 (S = 0.88, c/a > 1). The elastic constants C′ and C44 of these alloys decr...
متن کاملLattice softening in superconducting compositions of Ba(K)BiO3.
Temperature dependent x-ray absorption spectra investigation were measured for Ba(1-x)K(x)BiO3 (Bi L3-edge) with x =0.0, 0.25, 0.4, 0.5 and for BaPbO3 (Pb L3-edge). It was found that at low temperatures the Debye-Waller factor of the square diagonal Bi-Bi bond has the maximum value near the insulator-metal phase transition for the compound with x = 0.25 and x = 0.4. Temperature dependence of th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Physical Review B
سال: 1991
ISSN: 0163-1829,1095-3795
DOI: 10.1103/physrevb.44.11689