Local order around rare earth ions during the devitrification of oxyfluoride glasses
نویسندگان
چکیده
منابع مشابه
Local order around rare earth ions during the devitrification of oxyfluoride glasses.
Erbium L(3)-edge extended x-ray absorption fine structure (EXAFS) measurements were performed on rare earth doped fluorosilicate and fluoroborate glasses and glass ceramics. The well known nucleating effects of erbium ions for the crystallization of cubic lead fluoride (based on x-ray diffraction measurements) and the fact that the rare earth ions are present in the crystalline phase (as indica...
متن کاملNear-infrared luminescence of rare earth ions in oxyfluoride lead borate glasses and transparent glass-ceramic materials
Oxyfluoride lead borate glasses singly doped with Nd3+ and Er3+ ions have been studied before and after thermal treatment. The orthorhombic PbF2 crystallites are formed during thermal treatment, which was evidenced by X-ray diffraction analysis. Near-infrared luminescence spectra at 1.06 μm and 1.53 μm have been registered for samples before and after annealing, which correspond to the main F3/...
متن کاملYb-Sensitized Rare-Earth Doped Optical Glasses
The temperature e ect upon infrared-to-visible frequency upconversion uorescence emission in o -resonance infrared excited Yb-sensitized rare-earth doped optical glasses is theoretically and experimentally investigated. We have examined samples of Er3+/Yb-codoped Ga2S3:La2O3 chalcogenide glasses and germanosilicate optical bers, and Ga2O3:La2O3 chalcogenide and uoroindate glasses codoped with P...
متن کاملN I,1,11 1I Visible emission from rare earth ions in nanocrystal-containing glasses
Rare earth-doped glasses are of great interest for their optical and fluorescence properties. However, phononmediated non-radiative transitions are a major obstacle to their use and the quantum efficiencies are sensitive to the environment of the rare earth ion. Recently, complex glasses containing fluorides have been developed in which fluoride crystallites can be made to form with a high solu...
متن کاملGeS2–In2S3–CsI Chalcogenide Glasses Doped with Rare Earth Ions for Near- and Mid-IR Luminescence
Chalcogenide glass has been considered as a promising host for the potential laser gain and amplifier media operating in near- and mid-IR spectral region. In this work, the IR luminescence spectra of rare earth ions (Tm3+, Er3+, and Dy3+) doped 65GeS2-25In2S3-10CsI chalcogenide glasses were measured under the excitation of an 808 nm laser diode. To the best of our knowledge, it firstly provides...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Journal of Chemical Physics
سال: 2008
ISSN: 0021-9606,1089-7690
DOI: 10.1063/1.2943672