Location of Cu2+in CHA zeolite investigated by X-ray diffraction using the Rietveld/maximum entropy method

Location of Cu2+ in CHA zeolite investigated by X-ray diffraction using the Rietveld/maximum entropy method

Accurate structural models of reaction centres in zeolite catalysts are a prerequisite for mechanistic studies and further improvements to the catalytic performance. The Rietveld/maximum entropy method is applied to synchrotron powder X-ray diffraction data on fully dehydrated CHA-type zeolites with and without loading of catalytically active Cu(2+) for the selective catalytic reduction of NO x...

Fusion bonding of Si wafers investigated by x ray diffraction

the plain x-ray the diagnosis of the acute abdomen_

چکیده ندارد.

buckling of viscoelastic composite plates using the finite strip method

در سال های اخیر، تقاضای استفاده از تئوری خطی ویسکوالاستیسیته بیشتر شده است. با افزایش استفاده از کامپوزیت های پیشرفته در صنایع هوایی و همچنین استفاده روزافزون از مواد پلیمری، اهمیت روش های دقیق طراحی و تحلیل چنین ساختارهایی بیشتر شده است. این مواد جدید از خودشان رفتارهای مکانیکی ارائه می دهند که با تئوری های الاستیسیته و ویسکوزیته، نمی توان آن ها را توصیف کرد. این مواد، خواص ویسکوالاستیک دارند....

Phase determination and extension using X-ray multiple diffraction and the maximum-entropy method.

The extension of the phases of the structure factors of the organic crystal C(25)H(25)NO(2) from 77 starting individual phases using the maximum-entropy method is reported. These starting phases were determined from 90 experimental triplet phases calculated from 215 measured psi-scan three-beam and four-beam diffraction profiles obtained with a rotating-anode X-ray source, where the psi scans w...