Low-temperature Atmosphere-free Molten Salt Synthesis of NIR-shielding CsxWO3
نویسندگان
چکیده
منابع مشابه
LOW TEMPERATURE MOLTEN SALT SYNTHESIS OF NANO CRYSTALLINE MgAl2O4 POWDER
Abstract: composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nanopowder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-Teller (BET) techniques. It was demonstrated tha...
متن کاملLow temperature synthesis of CaZrO3 nanoceramics from CaCl2–NaCl molten eutectic salt
CaZrO3 nanoceramics were successfully synthesized at 700 C using the molten salt method, and the effects of processing parameters, such as temperature, holding time, and amount of salt on the crystallization of CaZrO3 were investigated. CaCl2, Na2CO3, and nano-ZrO2 were used as starting materials. On heating, CaCl2–NaCl molten eutectic salt provided a liquid medium for the reaction of CaCO3 an...
متن کاملlow temperature synthesis of cazro3 nanoceramics from cacl2–nacl molten eutectic salt
cazro3 nanoceramics were successfully synthesized at 700 c using the molten salt method, and the effects of processing parameters, such as temperature, holding time, and amount of salt on the crystallization of cazro3 were investigated. cacl2, na2co3, and nano-zro2 were used as starting materials. on heating, cacl2–nacl molten eutectic salt provided a liquid medium for the reaction of caco3 an...
متن کاملMolten Salt Synthesis of Calcium Hydroxyapatite Whiskers
Calcium hydroxyapatite (HA) whiskers and crystals were produced by the route of molten salt synthesis. The effects on whisker morphology of chosen flux, flux-to-HA ratio, synthesis temperature, and reaction time were investigated. The thermal stabilities of the produced whiskers were tested at 1300°C in an air atmosphere. A tentative X-ray diffraction pattern was proposed for the HA whiskers. M...
متن کاملElectrodeposition of Zinc From Low Temperature Molten Salt Electrolyte: Part I-Imidazole And Zinc-Chloride Electrolyte
Our R & D work was focused on the electro deposition of Zinc from imidazole as low temperature molten salt (LTMS) electrolyte with zinc chloride as a supporting salt at <100o C., without required controls from the previous existing non aqueous baths as well additive free system for the zinc deposition. Surface morphological studies and crystallographic orientation results were evaluated.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nano Advances
سال: 2017
ISSN: 2415-1386
DOI: 10.22180/na216