Magnetic Cation Distribution in Nanocrystalline Fe3O4 Spinel
Neutron diffraction study of nanostructured magnetite was performed at room temperature. The actual grain-size was determined from evaluation of X-ray diffraction profiles by the modified Williamson-Hall plot. The atomic structure parameters and the sublattice magnetic moments were determined using the Rietveld refinement of the neutron diffraction spectra. The sublattice magnetization at the o...
متن کاملMagnetic resonance in molybdenum spinel-like compounds
2014 Measurements of the magnetic resonance linewidth 0394H of molybdenum spinels are reported for both paramagnetic and ferromagnetic phases, with particular attention to the region near critical temperature. The magnetic resonance spectra have been measured in the temperature range from 10 K to 300 K with a standard Xband ESR spectrometer. It was shown that the characteristic temperature chan...
متن کاملSynthesis, Characterization, and Sensor Applications of Spinel ZnCo2O4 Nanoparticles
Spinel ZnCo₂O₄ nanoparticles were synthesized by means of the microwave-assisted colloidal method. A solution containing ethanol, Co-nitrate, Zn-nitrate, and dodecylamine was stirred for 24 h and evaporated by a microwave oven. The resulting solid material was dried at 200 °C and subsequently calcined at 500 °C for 5 h. The samples were characterized by scanning electron microscopy (SEM), trans...
متن کاملSynthesis and characterization of nanocrystalline spinel Zinc ferrite prepared by sol-gel auto-combustion technique
Sol–gel auto-combustion is a unique combination of the combustion and the chemical gelation processes. In this work, nanosize (d) powders with compositions of ZnFe2O4 were synthesized by sol–gel combustion method. The puffy, porous brown powders as-combusted was calcined at the temperature of 750–1000◦C for 4 h. These powders are characterized by X-ray diffraction and scanning electron microsco...
متن کاملMagnetic coupling among spinel iron oxide microparticles by Mössbauer spectroscopy
2014 Mössbauer spectra of hydrous spinel iron oxide colloids and their evolution with thermal treatment have been interpreted using a modified Weiss local field model. It is found that interparticle interactions overcome the single particle anisotropy energy. Existence of a crystalline texture within aggregates is suggested. J. Physique Lett. 46 (1985) L-437 L-443 15 mm 1985, Classification Phy...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics and Chemistry of Solids
سال: 2008
ISSN: 0022-3697
DOI: 10.1016/j.jpcs.2007.11.005