Magnetic Properties of FePt based Nanocomposite Thin Films Grown on Low Cost Substrates
نویسندگان
چکیده
منابع مشابه
Improvement of Magnetic Properties and Texture of FePt Thin Films on MgO Substrates by Sn Addition
In this work, we studied the effects of Sn addition on the ordering temperature of FePt thin film. The coercivity of FePtSn film was about 1000 Oe greater than the coercivity of FePt film for an annealing temperature of 600C. Therefore, Sn addition was effective in promoting the L10 ordering and in reducing the ordering temperature of the FePt film. From our X-ray diffraction results, we found ...
متن کاملMagnetic Properties of Nanostructured CoPt and FePt Thin Films
Polycrystalline MgO underlayer films lead to different preferred orientations of 10 CoPt and FePt films after the annealing process, depending on the thickness of 10 films. 10 films with a thickness greater than 20 nm revealed mostly 10 [100] fiber texture and consequently in-plane anisotropy as determined by magnetic hysteresis. Strong perpendicular anisotropy due to the 10 [001] fiber texture...
متن کاملThermal Oxidation Times Effect on Structural and Morphological Properties of Molybdenum Oxide Thin Films Grown on Quartz Substrates
Molybdenum oxide (α-MoO)thin films were prepared on quartz and silicon substrates by thermal oxidation of Mo thin films deposited using DC magnetron sputtering method. The influence of thermal oxidation times ranging from 60-240 min on the structural and morphological properties of the preparedfilms was investigated using X-ray diffraction, Atomic force microscopy and Fourier transform infrared...
متن کاملEffects of Ag underlayers on the microstructure and magnetic properties of epitaxial FePt thin films
In this work Ag underlayers, with a slightly larger unit cell than FePt, were found not only to induce epitaxial growth of the FePt films but also to reduce the FePt ordering temperature. Without using the Ag underlayer, the FePt film deposited onto the Si substrate was fcc disordered. By the use of the Ag underlayer, it was observed that the FePt unit cells were expanded in the film plane. Thi...
متن کاملEnhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates
Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Physics Procedia
سال: 2014
ISSN: 1875-3892
DOI: 10.1016/j.phpro.2014.10.032