Magnetic properties of (misch metal, Nd)-Fe-B melt-spun magnets
نویسندگان
چکیده
منابع مشابه
Effect of Post-Sintering Annealing Treatment on Magnetic Properties of Some Nd Fe b Based Magnets
Effects of post-sintering annealing treatment between 300 and 1000ºC for up to 8 hrs time periods followed by either furnace cooling (FC) or air-cooling (AC) on the hard magnetic properties of some Nd-Fe-B based sintered magnets was investigated. It was shown that the intrinsic coercivity (Hci), second quadrant demagnetization loop shape and thus the energy density (BH)max varied considerably a...
متن کاملMagnetic properties of Nd-Fe-B/α-Fe multi-layered thick film magnets
Nd-Fe-B/α-Fe multi-layered nanocomposite film-magnets were prepared from a rotating Nd2.6Fe14B/α-Fe composite target by the pulse laser deposition method with a NdYAG laser (λ=355 nm). The prepared film-magnets were composed of approximately 800 layers with the thickness of about several tens nanometre, and exhibited hard magnetic properties after annealing. The laser power for the ablation of ...
متن کاملMicrostructure and magnetic domain structure of boron - enriched Nd 2 ( FeCo ) 14 B melt - spun ribbons
Heat treated melt-spun ribbons of (Nd La) Fe Co Nb B have been studied systematically by supercon-ducting quantum interference device (SQUID) magnetometry, conventional transmission electron microscopy (CTEM) and Lorentz transmission electron microscopy (LTEM). The sample's microstructure grew from an amorphous state through a partially crystallized state at 6503C, and "nally to a fully crystal...
متن کاملMagnetic properties and synthesis conditions of Nd2Fe23B3 melt-spun alloy
The formation of amorphous and crystalline state of the Nd2Fe23B3 alloy from melt-spun ribbon is presented. The synthesis conditions are investigated combining DSC, X-ray diffraction and thermomagnetic analysis. The thermomagnetic analysis is found to be very useful to optimize the synthesis process. Comparison of these results enables to discuss the thermal stability of both the amorphous and ...
متن کاملControlling the crystallization and magnetic properties of melt-spun Pr2Fe14BÕa-Fe nanocomposites by Joule heating
Pr2Fe14B/a-Fe based nanocomposites have been prepared through crystallization of melt-spun amorphous Pr7Tb1Fe85Nb0.5Zr0.5B6 ribbons by means of ac Joule heating while simultaneously monitoring room-temperature electrical resistance R. The R value shows a strong variation with respect to applied current I, and is closely related to the amorphous-to-nanocrystalline phase transformation. The curve...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: AIP Advances
سال: 2017
ISSN: 2158-3226
DOI: 10.1063/1.4973846