Magnetic unmixing of first-order reversal curve diagrams using principal component analysis
نویسندگان
چکیده
منابع مشابه
Magnetic Properties of Fe49Co33Ni18Nanowire ArraysStudied by First-Order Reversal Curve Diagrams
Fe49Co33Ni18 nanowire arrays (175 nm in diameter and lengths ranging from 5 to 32μm) were fabricated into nanopores of hard-anodized aluminum oxide templates using pulsed ac electrodeposition technique. Hysteresis loop measurements indicated that increasing the length decreases coercivity and squareness values (from 274 Oe and 0.58 to200 Oe and 0.105, respective...
متن کاملmagnetic properties of fe49co33ni18nanowire arraysstudied by first-order reversal curve diagrams
fe49co33ni18 nanowire arrays (175 nm in diameter and lengths ranging from 5 to 32μm) were fabricated into nanopores of hard-anodized aluminum oxide templates using pulsed ac electrodeposition technique. hysteresis loop measurements indicated that increasing the length decreases coercivity and squareness values (from 274 oe and 0.58 to200 oe and 0.105, respectively), indicating the increase in m...
متن کاملFirst-order reversal-curve diagrams and reversible magnetization
First-order reversal curve ~FORC! diagrams have recently been used for the characterization of magnetic systems in both geology and physics. However, the FORC distribution involves a mixed second derivative which reduces the reversible component of the magnetization to zero. As a result, the FORC distribution is not properly normalized. Furthermore, the calculation of the FORC distribution beco...
متن کاملFirst-order reversal curve diagrams and thermal relaxation effects in magnetic particles
We have recently developed a technique for characterizing the magnetic components within natural particle assemblages. This technique is based on the transformation of magnetization data from first-order reversal curves (FORCs) into contour plots of a 2-D distribution function (FORC diagrams). FORC diagrams are useful for obtaining information about switching fields and interactions in magnetic...
متن کاملIncreasing the efficiency of paleointensity analyses by selection of samples using first-order reversal curve diagrams
[1] The global paleointensity database is restricted by the high failure rate of paleointensity analyses. Excluding thermal alteration, failure is usually caused by the presence of multidomain grains and interactions among grains, two properties that can be identified using first-order reversal curve (FORC) diagrams. We measured FORC diagrams on sister samples of about 200 samples that had been...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Geochemistry, Geophysics, Geosystems
سال: 2015
ISSN: 1525-2027
DOI: 10.1002/2015gc005909