Martensitic Transformation and Crystalline Structure of Ni50Mn50−xSnx Melt-Spun Heusler Alloys
نویسندگان
چکیده
منابع مشابه
Martensitic Transformation in Ni-Mn-Sn-Co Heusler Alloys
Thermal and structural austenite to martensite reversible transition was studied in melt spun ribbons of Ni50Mn40Sn5Co5, Ni50Mn37.5Sn7.5Co5 and Ni50Mn35Sn10Co5 (at. %) alloys. Analysis of X-ray diffraction patterns confirms that all alloys have martensitic structure at room temperature: four layered orthorhombic 4O for Ni50Mn40Sn5Co5, four layered orthorhombic 4O and seven-layered monoclinic 14...
متن کاملMartensitic Transformation in Microcrystalline Melt-Quenched Fe-Ni Alloys
The features of martensite transformation in Fe (31 32)% Ni melt-quenched alloys are considered. The meltquenching was realized by spinning technique with variable parameters. The influence of the melt-quenching on structural and kinetics transformation parameters is revealed. In particular Ms point is shown to decrease but volume percentage of athermal martensite is found to be invariable with...
متن کاملHard magnetic properties of melt-spun Mn-Al-C alloys
Structural and magnetic characterization of Mnx−yAl100−x−yC2y (x = {50, 55}; y = {0, 1}) melt-spun ribbons is reported. To obtain the metastable ferromagnetic τ-phase, rapidly solidified alloys were annealed either in a vacuum furnace at 823 K or directly in the vibrating sample magnetometer under applied magnetic field. Optimal magnetic properties were demonstrated by Mn54Al44C2 samples proved...
متن کاملRecrystallization Phenomena in Melt-Spun (Fe100- xVx)75P15C10 Alloys
(Fe100-xVx)75P15C10 (x=0, 5, 10 and 15) semiamorphous alloys were prepared by the melt spinning technique and their structural, thermal and magnetic properties were investigated. The structure of the alloys was studied by X-ray diffraction (XRD) for annealing temperatures of 400 oC to 650 oC within a 30 minute annealing time. The XRD patterns show that the samples contain a BCC structure for te...
متن کاملEffects of Annealing on the Martensitic Transformation of Ni-Based Ferromagnetic Shape Memory Heusler Alloys and Nanoparticles
We report on the effects of annealing on the martensitic phase transformation in the Ni-based Heusler system: Mn50Ni40Sn10 and Mn50Ni41Sn9 powder and Co50Ni21Ga32 nanoparticles. For the powdered Mn50Ni40Sn10 and Mn50Ni41Sn9 alloys, structural and magnetic measurements reveal that post-annealing decreases the martensitic transformation temperatures and increases the transition hysteresis. This m...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Crystals
سال: 2020
ISSN: 2073-4352
DOI: 10.3390/cryst10100853