Mean stress effect under Multi-Axial High Cycle Fatigue loading for cast A356-T6 alloy
نویسندگان
چکیده
منابع مشابه
High Cycle Fatigue Property of Carburized 20Cr Gear Steel under Axial Loading
Abstract: The high cycle fatigue property of carburized 20Cr gear steel was experimentally investigated under axial loading with a stress ratio of zero. The test results show that this steel exhibits gradually decreasing S-N characteristics, and the fatigue strength corresponding to 109 cycles is about 455 MPa. Based on the observation of fracture surfaces, the interior inclusion fisheye-induce...
متن کاملEffect of Low Cycle Fatigue Predamage on Very High Cycle Fatigue Behavior of TC21 Titanium Alloy
The effect of low cycle fatigue (LCF) predamage on the subsequent very high cycle fatigue (VHCF) behavior is investigated in TC21 titanium alloy. LCF predamage is applied under 1.8% strain amplitude up to various fractions of the expected life and subsequent VHCF properties are determined using ultrasonic fatigue tests. Results show that 5% of predamage insignificantly affects the VHCF limit du...
متن کاملPorosity Control and Fatigue Behavior in A356-T61 Aluminum Alloy
Much work has been done, in recent years, to characterize the factors that cause porosity in aluminum castings, and to analyze the impact of porosity or microstructural parameters on fatigue life. What has yet to be done is systematically separate out the effects of dendrite arm spacing and largest pore size from each other, and from the underlying chemical and process parameters that influence...
متن کاملImpact Properties of A356-T6 Alloys
The Charpy impact energy of A356 alloys has been measured. Instrumented Charpy impact tests have been conducted at 25, 100, 150, and 200 ~ The Charpy specimens were machined from plate castings or tapered cylindrical castings. The plates were produced in sand molds, and tapered cylinders were produced in water-cooled copper molds. Both unmodified and strontium-modified castings were tested. The...
متن کاملRatcheting crystal plasticity modeling in microstructure of magnesium alloy under stress-controlled cyclic tensile loading with non-zero mean stress
Todays, the requirement of lowering the vehicle weight for the reduction of the fuel consumption and emissions, one of the methods considered by designers is to use the ligh magnesium alloy under cylclic loadings. In this article, considering the microstructure of the AZ91D magnesium alloy, its crystalline structure, a model for predicting the ratcheting behavior of this alloy was adapted and v...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATEC Web of Conferences
سال: 2014
ISSN: 2261-236X
DOI: 10.1051/matecconf/20141204025