Mechanical Characteristics of CF Laminated Prepreg with UV-thermal Dual Curable Epoxy Resin
نویسندگان
چکیده
منابع مشابه
Synthesis and characterization of novel dual UV/thermal curable epoxy rosinate
Rosin has a comprehensive application in adhesives, printing inks, protective coatings, rubbers and pharmaceutical. In this work, novel dual UV/thermal curable epoxy rosinate was synthesized by esterification reaction between epoxy resin and purified rosin. This product was evaluated by FT-IR spectroscopy techniques and acid number. UV curable resin was formulated for UV curing ability by benzo...
متن کاملStudy the curing behavior and mechanical properties of Pigmented UV curable epoxy acrylate monomers
The formulations contained different acrylate monomer with different structure and functionalities and TiO2, were applied to obtain pigmented acrylic films by UV exposure. The conversion and mechanical characteristic were correlated. The results showed that there is a significant interaction between pigment, reactive diluents’ type and mechanical properties of coatings. It seems that cured film...
متن کاملMechanical and Thermal Properties of Chemically Modified Epoxy Resin
Diglycidyl ether of bisphenol-A (DGEBA), having number average molecular weight (Mn) 375, was modified by incorporating the hydroxyl terminated polybutadiene (HTPB) based prepolymer using isophorone diisocyanate as a coupling agent. To increase the compatibility between the epoxy resin and HTPB part, polar groups were introduced in the later to achieve physical and chemical interactions between...
متن کاملThermal Rheological Analysis of Cure Process of Epoxy Prepreg
The cure process of epoxy prepreg used as composite pipe joints was studied by means of differential scanning calorimetry (DSC), Bohlin Rheometer and other techniques. Isothermal DSC measurements were conducted between 110 and 220 C, at 10 C intervals. The results show that the complete cure reaction could be achieved at 220 C. The isothermal cure process was simulated with the four-parameter a...
متن کاملThermal Conductivity and Viscoelastic Properties of UV-curable Urethane Acrylate Reinforced with Modified Al2O3 Nanoparticles
In this study, UV-curable urethane acrylate UA synthesized and then characterized by FTIR and HNMR. For better dispersion of nanoparticles in polymeric matrix, nano Al2O3 was modified by silane coupling agent and then its nanocomposites were prepared. The characteristics of synthesized nanocomposites were analyzed by TGA, DMA and infrared thermography. The results signify that adding nano Al2O3...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Textile Coloration and Finishing
سال: 2017
ISSN: 1229-0033
DOI: 10.5764/tcf.2017.29.1.37