Mechanical response of aluminum 7075 with heat treatment and exfoliation corrosion

The present investigation was focussed to evaluate the mechanical properties of AA7075 subjected corrosion and heat treatment. Exfoliation has been used infuse rapid on material coupled with high temperature subsequent low-temperature aging (HLA). It found that localized pit formation occurs HLA exposure durations substantial inter-granular changes cracks. Significant reduction in observed HLA-treated samples corrosion. material’s stiffness increased due HLA, again within corrosive environment, a decreasing trend immersion durations. A series simple one-dimensional linear polynomial equations were developed determine