MECHANISM OFMOISTURE SORPTION HYSTERESIS OF HARDEND CEMENT PASTE
نویسندگان
چکیده
منابع مشابه
Hysteresis from Multiscale Porosity: Modeling Water Sorption and Shrinkage in Cement Paste
Article is made available in accordance with the publisher's policy and may be subject to US copyright law. Please refer to the publisher's site for terms of use. The MIT Faculty has made this article openly available. Please share how this access benefits you. Your story matters. Cement paste has a complex distribution of pores and molecular-scale spaces. This distribution controls the hystere...
متن کاملDecalcification shrinkage of cement paste
Decalcification of cement paste in concrete is associated with several modes of chemical degradation including leaching, carbonation and sulfate attack. The primary aim of the current study was to investigate the effects of decalcification under saturated conditions on the dimensional stability of cement paste. Thin (0.8 mm) specimens of tricalcium silicate (C3S) paste, white portland cement (W...
متن کاملSorption hysteresis of benzene in charcoal particles.
Charcoal is found in water, soil, and sediment where it may act as a sorbent of organic pollutants. The sorption of organic compounds to natural solids often shows hysteresis. The purpose of this study was to determine the source of pronounced hysteresis that we found in the sorption of a hydrophobic compound (benzene) in water to a maple-wood charcoal prepared by oxygen-limited pyrolysis at 67...
متن کاملOnset of cohesion in cement paste.
It is generally agreed that the cohesion of cement paste occurs through the formation of a network of nanoparticles of a calcium-silicate-hydrate ("C-S-H"). However, the mechanism by which these particles develop this cohesion has not been established. Here we propose a dielectric continuum model which includes all ionic interactions within a dispersion of C-S-H particles. It takes into account...
متن کاملDrying Shrinkage Mechanisms in Portland Cement Paste
The shrinkage mechanisms of portland cement paste were investigated from shrinkage, weight loss, and pore structure measurements using nitrogen sorption and mercury intrusion porosimetry (MIP). Thin samples (2.3 mm) of well-hydrated (165 d) pastes of 0.4 and 0.6 water-to-cement (W/C) ratios were dried directly from saturated surface dry state to 75%, SO%, 11%, and 0% relative humidity (rh). Fro...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Cement Science and Concrete Technology
سال: 2010
ISSN: 0916-3182,2187-3313
DOI: 10.14250/cement.64.96