Micro- and nano-structural evolutions in white Portland cement/pulverized fuel ash cement pastes due to deionized-water leaching
نویسندگان
چکیده
منابع مشابه
Micro- and nano-structural evolutions in white Portland cement/pulverized fuel ash cement pastes due to deionized-water leaching
Thin slices of white Portland cement-low calcium pulverized fuel ash (pfa) blended cement pastes containing 30 or 50% pfa were leached progressively in de-ionized water. The paste with 50% pfa was aged 13 years prior to leaching and those with 30% pfa were aged 1 and 13 years. Pastes were leached for up to 75 days and were characterized using thermal analysis, X-ray diffraction, analytical scan...
متن کاملCompressive strength of Portland cement pastes and mortars containing Cu-Zn nano-ferrite
This study is concerned with the synthesizing of Cu-Zn nano-ferrite particles in the laboratory applying simple techniques. The morphology of the synthesized nano-particles was analyzed using Transmission Electron Microscopy (TEM), and the minerals were identified using X-ray diffraction (XRD). The nano material was used to replace 1- 4 percent by weight of Portland cement in cement pastes and ...
متن کاملCompressive strength of Portland cement pastes and mortars containing Cu-Zn nano-ferrite
This study is concerned with the synthesizing of Cu-Zn nano-ferrite particles in the laboratory applying simple techniques. The morphology of the synthesized nano-particles was analyzed using Transmission Electron Microscopy (TEM), and the minerals were identified using X-ray diffraction (XRD). The nano material was used to replace 1- 4 percent by weight of Portland cement in cement pastes and ...
متن کامل(Micro)-structural comparison between geopolymers, alkali-activated slag cement and Portland cement
Concurrently to research conducted on ordinary Portland cement (PC), new types of binders were developed during the last decades. These are formed by alkali-activation of metakaolin or ground-granulated blast furnace slag (GGBFS) and are named, respectively, geopolymers (GP) or alkali-activated slag (AAS). Four different cementitious materials were synthesised: PC, AAS, GP, and a mix GP-AAS and...
متن کاملcompressive strength of portland cement pastes and mortars containing cu-zn nano-ferrite
this study is concerned with the synthesizing of cu-zn nano-ferrite particles in the laboratory applying simple techniques. the morphology of the synthesized nano-particles was analyzed using transmission electron microscopy (tem), and the minerals were identified using x-ray diffraction (xrd). the nano material was used to replace 1- 4 percent by weight of portland cement in cement pastes and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Cement and Concrete Research
سال: 2018
ISSN: 0008-8846
DOI: 10.1016/j.cemconres.2017.10.014