Ordered periodic microlattices with densities from 0.5 mg/cm3 to 500 mg/cm3 are fabricated by depositing various thin film materials (Au, Cu, Ni, SiO2, poly(C8H4F4)) onto sacrificial polymer lattice templates. Young’s modulus and strength are measured in compression and the density scaling is determined. At low relative densities, recovery from compressive strains of 50% and higher is observed,...
متن کاملarchitecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولdetermination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولEffect of nanozeolite 13X on thermal and mechanical properties of Polyurethane nanocomposite thin films
Polyurethane/zeolite 13X nanocomposite films were fabricated using solution casting method. The synthesized nanocomposite films were structurally characterized using SEM, TGA and tensile analysis. SEM images showed appropriate distribution of nanocrystalline zeolite particles within polyurethane matrix. Better thermal stability of nanocomposite films in comparison to neat polyurethane was shown...
متن کاملEffect of nanozeolite 13X on thermal and mechanical properties of Polyurethane nanocomposite thin films
Polyurethane/zeolite 13X nanocomposite films were fabricated using solution casting method. The synthesized nanocomposite films were structurally characterized using SEM, TGA and tensile analysis. SEM images showed appropriate distribution of nanocrystalline zeolite particles within polyurethane matrix. Better thermal stability of nanocomposite films in comparison to neat polyurethane was shown...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: APL Materials
سال: 2013
ISSN: 2166-532X
DOI: 10.1063/1.4818168