Microstructural Effect Controlling Exhaustion of Ductility in Extremely Low-Cycle Fatigue.
نویسندگان
چکیده
منابع مشابه
An efficient life prediction methodology for low cycle fatigue–creep based on ductility exhaustion theory
Low cycle fatigue–creep is the main reason for the failures of many engineering components under high temperature and cyclic loading. Based on the exhaustion of the static toughness and dissipation of the plastic strain energy during fatigue failure, a new low cycle fatigue–creep life prediction model that is consistent with the fatigue–creep damage mechanism and sensitive to the fatigue damage...
متن کاملEffect of Low Cycle Fatigue Predamage on Very High Cycle Fatigue Behavior of TC21 Titanium Alloy
The effect of low cycle fatigue (LCF) predamage on the subsequent very high cycle fatigue (VHCF) behavior is investigated in TC21 titanium alloy. LCF predamage is applied under 1.8% strain amplitude up to various fractions of the expected life and subsequent VHCF properties are determined using ultrasonic fatigue tests. Results show that 5% of predamage insignificantly affects the VHCF limit du...
متن کاملEffect of occupational exposure to extremely low frequency electromagnetic fields on level of thyroid hormones effective on fatigue
Background: The aim of this study was to assess exposure to extremely low frequency electromagnetic fields (ELF-EMFs) and its effects on secretion of thyroid hormones associated with symptoms of fatigue on electric arc welding workers. Methods: This study was carried out on two groups including 35 welders (as exposed) and 35 non-welders (as control). Extremely low frequency electromagnetic fie...
متن کاملLinkage between Ductile Fracture and Extremely Low Cycle Fatigue of Inconel 718 under Multiaxial Loading Conditions
Ductile fracture and extremely low cycle fatigue (ELCF) [1] are two common failure modes in aircraft engines and turbomachinery designs [2]; however, the linkage between these two failure modes under multi-axial loading conditions has never been systematically studied. Inconel 718 (IN718) is one type of high temperature alloys widely used in turbomachines. Specially designed specimens and tests...
متن کاملLow Cycle Fatigue Simulation of Valve Bridge Region in Cylinder Head Based on Critical Plane Model
The reason of this study is low cycle failure of cast iron cylinder head during the E5 standard durability test. The goal of the present investigation is durability test simulation and low cycle fatigue life evaluation of cast iron cylinder head. With uncouple structural analysis, preloads, thermal and mechanical load and boundary conditions are prescribed to finite element model of the cylinde...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1991
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.57.2879