Microstructural Evolution during DPRM Process of Semisolid Ledeburitic D2 Tool Steel
نویسندگان
چکیده
منابع مشابه
Microstructural Evolution during DPRM Process of Semisolid Ledeburitic D2 Tool Steel
Semisolid metal processing is a relatively new technology that offers several advantages over liquid processing and solid processing because of the unique behaviour and characteristic microstructure of metals in this state. With the aim of finding a minimum process chain for the manufacture of high-quality production at minimal cost for forming, the microstructural evolution of the ledeburitic ...
متن کاملMicrostructural Evolution of X45CrNiW189 Valve Steel During Hot Deformation
The hot compression tests were carried on X45CrNiW189 valve steel (X45) in the temperature range of 1000– 1200 °C and the strain rate range of 0.004 – 0.5 s-1 in order to study the high temperature softening behavior of this steel. For the exact prediction of flow stress, the effective stress-effective strain curves were obtained from experiments under various conditions. On the basis of experi...
متن کاملApplications of Impedance Plane and Magnetic Differential Permeability in Microstructural Characterization of AISI D2 Tool Steel
Two nondestructive electromagnetic/magnetic techniques including hysteresis loop and eddy current methodologies have been used to characterize microstructural changes of AISI D2 cold work tool steel as a result of quench and tempering treatments. To measure the fraction retained austenite in quenched microstructure, six specimens were austenitized in the range of 1000-1130 °C. Samples austenit...
متن کاملMicrostructural Properties of Semisolid Welded Joints for AISI D 2 Tool Steel
The aim of this study is to investigate experimentally the microstructural evolution of the joints using ledeburitic AISI D2 Tool Steel parts. The application of a new process of the semisolid joining of two parts of AISI D2 cold-work tool steel is proposed using a partial remelting method. Samples were heated in an argon atmosphere up to 1300°C and held for 10 minutes. Metallographic analyses ...
متن کاملmicrostructural evolution of x45crniw189 valve steel during hot deformation
the hot compression tests were carried on x45crniw189 valve steel (x45) in the temperature rangeof 1000– 1200 °c and the strain rate range of 0.004 – 0.5 s-1 in order to study the high temperaturesoftening behavior of this steel. for the exact prediction of flow stress, the effective stress-effectivestrain curves were obtained from experiments under various conditions. on the basis of experimen...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Scientific World Journal
سال: 2013
ISSN: 1537-744X
DOI: 10.1155/2013/828926