Microstructural Evolution of a Pearlitic Steel Subjected to Thermomechanical Processing

Microstructural Evolution of X45CrNiW189 Valve Steel During Hot Deformation

The hot compression tests were carried on X45CrNiW189 valve steel (X45) in the temperature range of 1000– 1200 °C and the strain rate range of 0.004 – 0.5 s-1 in order to study the high temperature softening behavior of this steel. For the exact prediction of flow stress, the effective stress-effective strain curves were obtained from experiments under various conditions. On the basis of experi...

Effect of Thermomechanical Processing on the Microstructure and Mechanical Properties of a Duplex Stainless Steel

Duplex stainless steels (DSSS) have a microstructure composed of ferrite and austenite phases that gives them a very good combination of mechanical and corrosion properties. These steels are desirable for many applications in the chemical and petrochemical industries. In the present study, a type of stainless steel was cast, solution annealed at 1200°C for 60 min and then quenched in water. Ini...

Microstructural Evolution and Mechanical Properties of Ultrafine/nano Structured AISI 321 Stainless Steel Produced by Thermo-mechanical Processing

The mechanical properties and microstructural developments of 321 stainless steel during thermomechanical process were investigated. The repetitive cold rolling and subsequent annealing were conducted to achieve nanocrystalline structure in an AISI 321 stainless steel. Heavily cold rolling at −20°C was conducted to form martensite in metastable austenitic steel. The process was followed by anne...

Electropulse-induced microstructural evolution in a ferriticpearlitic 0.14% C steel

microstructural evolution of x45crniw189 valve steel during hot deformation

the hot compression tests were carried on x45crniw189 valve steel (x45) in the temperature rangeof 1000– 1200 °c and the strain rate range of 0.004 – 0.5 s-1 in order to study the high temperaturesoftening behavior of this steel. for the exact prediction of flow stress, the effective stress-effectivestrain curves were obtained from experiments under various conditions. on the basis of experimen...