Microstructural origins of cement paste degradation by external sulfate attack
نویسندگان
چکیده
منابع مشابه
Multi-mode X-ray Study of Sodium and Magnesium Sulfate Attack on Portland Cement Paste
Sulfate attack is potentially one of the most damaging forms of degradation affecting portland cement-based materials. However, despite over six decades of study, considerable uncertainty remains in optimally selecting and proportioning materials for sulfate resistance, and current understanding of the actual mechanisms of degradation in sulfate environments remains incomplete. In this research...
متن کاملPhysical Origins of Thermal Properties of Cement Paste
Article is made available in accordance with the publisher's policy and may be subject to US copyright law. Please refer to the publisher's site for terms of use. The MIT Faculty has made this article openly available. Please share how this access benefits you. Your story matters. Despite the ever-increasing interest in multiscale porous materials, the chemophysical origin of their thermal prop...
متن کاملSimulation of Expansion in Cement Based Materials Subjected to External Sulfate Attack
Sulfate attack in concrete structures is considered to be among the major durability concerns in civil infrastructure systems. Proper modeling techniques can help us understand the influence of aggressive environments on the concrete performance more readily and accurately. Such an understanding improves the decision making process in every stage of construction and maintenance and will help in...
متن کاملDecalcification shrinkage of cement paste
Decalcification of cement paste in concrete is associated with several modes of chemical degradation including leaching, carbonation and sulfate attack. The primary aim of the current study was to investigate the effects of decalcification under saturated conditions on the dimensional stability of cement paste. Thin (0.8 mm) specimens of tricalcium silicate (C3S) paste, white portland cement (W...
متن کاملThermodynamic Modeling of the Effects of Wollastonite-Silica Fume Combination in the Cement Hydration and Sulfate Attack
Sulfate attack is a series of physico-chemical reactions between hardened cement paste and sulfate ions. Sulfate ion penetration into the hydrated cement results in the formation of voluminous and deleterious phases such as gypsum and ettringite which are believed to cause deterioration and expansion of concrete. Concrete deterioration due to sulfate attack depends on many parameters, however, ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Construction and Building Materials
سال: 2015
ISSN: 0950-0618
DOI: 10.1016/j.conbuildmat.2015.07.186