Microstructure and Mechanical Properties of High-Strength Low-Carbon Bainitic Steels with Enhanced Deformability
نویسندگان
چکیده
منابع مشابه
High-Strength Bainitic Steels
With careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thin films of stable retained austenite have exhibited impressive combinations of strength and toughness in highsilicon bainitic steels. The silicon suppresses the precipitation of brittle cementite leading to an improvement in toughness. The essential principles governing the optimisatio...
متن کاملThe effects of chemical composition variations on microstructure and mechanical properties of nanostructured, low temperature bainitic steels
Bainitic transformation at low transformation temperatures leads to a microstructure involving fine plates of bainitic ferrite and thin films of retained austenite. This microstructure has shown ultimate tensile strength of about 2.2 GPa, noticeable uniform elongation in the range of 5 to 30%, hardness values of about 600 to 670 HV and impact toughness in the range of 30 to 40 MPa m1/2. With ca...
متن کاملhigh-strength bainitic steels
with careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thinfilms of stable retained austenite have exhibited impressive combinations of strength and toughness in highsiliconbainitic steels. the silicon suppresses the precipitation of brittle cementite leading to an improvement intoughness. the essential principles governing the optimisation o...
متن کاملEffect of Mo Content on Microstructure and Property of Low-Carbon Bainitic Steels
In this work, three low-carbon bainitic steels, with different Mo contents, were designed to investigate the effects of Mo addition on microstructure and mechanical properties. Two-step cooling, i.e., initial accelerated cooling and subsequent slow cooling, was used to obtain the desired bainite microstructure. The results show that the product of strength and elongation first increases and the...
متن کاملthe effects of chemical composition variations on microstructure and mechanical properties of nanostructured, low temperature bainitic steels
bainitic transformation at low transformation temperatures leads to a microstructure involving fine plates of bainitic ferrite and thin films of retained austenite. this microstructure has shown ultimate tensile strength of about 2.2 gpa, noticeable uniform elongation in the range of 5 to 30%, hardness values of about 600 to 670 hv and impact toughness in the range of 30 to 40 mpa m1/2. with ca...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Korean Journal of Materials Research
سال: 2013
ISSN: 1225-0562
DOI: 10.3740/mrsk.2013.23.8.423