Tribological coatings made of MoS2 and WSe2 phases and their corresponding combinations with tungsten carbide (WC) were prepared by non-reactive magnetron sputtering of individual targets of similar composition. A comparative tribological analysis of these multiphase coatings was done in both ambient air (30-40% relative humidity, RH) and dry nitrogen (RH<7%) environments using the same tribome...

Tribological behavior of sputter-deposited MoSX/Ni coatings

AbstractSputtered MoS2 coatings have been mostly used as a solid lubricant. In this investigation, MoSx/Ni composite coatings with Ni contents varying from 0 to 22 % were deposited onto steel substrate using a DC magnetron sputter process. The MoS2/Ni ratio in the coatings was controlled by sputtering the composite targets. The composition, microstructure, and mechanical properties of the...

Nanocomposite Based Multifunctional Coatings

TiC-based nanocomposite coatings as electrical contacts

This Thesis concerns the advanced surface engineering of novel TiC-based nanocomposite and AgI electrical contact materials. The objective is to make industrially applicable coatings that are electrically conductive and wear-resistant, and have a low coefficient of friction. I have studied electrical contact systems consisting of a Cu substrate with a Ni diffusion barrier and loading support, a...

Microstructure and mechanical properties of nanocomposite (Ti,Si,Al)N coatings

In this work (Ti,Si,Al)N films were deposited using only rf or a combination of rf and d.c. reactive magnetron sputtering. Chemical composition, thickness, film structure and mechanical properties of the films were investigated by means of Rutherford backscattering (RBS), electron microprobe analysis (EPMA), ball-cratering, X-ray diffraction (XRD) and ultramicroindentation, respectively. All sa...