Microwave Dielectric Properties of BiMg2VO6 Ceramic with Low Sintering Temperature
نویسندگان
چکیده
منابع مشابه
LOW-TEMPERATURE SINTERING AND MICROWAVE DIELECTRIC PROPERTIES OF (Zn0.65Mg0.35)TiO3-CaTiO3 CERAMICS WITH H3BO3 ADDITION
Low-melting H3BO3, acting as sintering aid, was used to reduce the sintering temperature of 5 wt.% CaTiO3-doped (Zn0.65Mg0.35)TiO3 ceramics. The sintering behaviors, microstructures and microwave dielectric properties with different amounts of H3BO3 addition were investigated. The results showed that H3BO3 additive was very effective for lowering the sintering temperature and improving the bulk...
متن کاملHigh Temperature Microwave Dielectric Properties of Ceramic Nano and Micropowders
The problem of microwave enhanced mass transport in solids remains an area of great interest and continued research in the microwave processing of materials. Many researchers have reported that microwave sintering of materials reduces the time and often the temperature of the sintering procedure [1]. The mechanisms of the mass transport enhancement phenomenon by microwaves termed “Microwave Eff...
متن کاملStructural and Dielectric Properties of Glass – Ceramic Substrate with Varied Sintering Temperatures
The main requirements of microwave circuit technology for wireless applications are a com‐ bination of high performance circuit, high integration density and frequency stability with a cost effective price [1-2]. Ceramic technology is particularly well suited to these require‐ ments due to the superior performance of their electrical, electromechanical, dielectric and thermal properties in orde...
متن کاملSintering properties of zirconia-based ceramic composite
This study examines the effects of different ZrB2 content on various mechanical properties and electrical conductivity of ZrB2/Y-TZP composite. Composites with ZrB2 content of up to 20 wt-% were particularly beneficial at the lower sintering temperature range by achieving greater densification and better hardness than Y-TZP monolith. In contrast to the trends estimated from rule of mixture, the...
متن کاملNovel ultra-low temperature co-fired microwave dielectric ceramic at 400 degrees and its chemical compatibility with base metal
A novel NaAgMoO4 material with spinel-like structure was synthesized by using the solid state reaction method and the ceramic sample was well densified at an extreme low sintering temperature about 400°C. Rietveld refinement of the crystal structure was performed using FULLPROF program and the cell parameters are a = b = c = 9.22039 Å with a space group F D -3 M (227). High performance microwav...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Inorganic Materials
سال: 2015
ISSN: 1000-324X
DOI: 10.15541/jim20140298