Mitigation of uncommon peel-off defects in galvanized steel sheets
نویسندگان
چکیده
منابع مشابه
Studies on defects in galvanized coating on steel wire
Causes for deposition of defective galvanized coating (lumpy deposition of coating during hot dip galvanizing) of carbon-steel wire have been investigated. It is established that the lumpy deposition is caused due to segregation of silicon on the surface of steel wire. Due to this change in composition of the steel at surface, the regions get modified and lie in Sandelin hyper reactive zone. Th...
متن کاملCorrosion of Galvanized Steel in Soils
The results of measurements of the corrosion of galvanized steel and of bare steel and zinc as reference materials after exposure to different soil conditions for a maximum of 13 years are reported. The magnitude and progress of corrosion of galvanized steel as determined by weight loss and pitting is interpreted in terms of the environmental conditions to which the specimens were exposed. From...
متن کاملDetermination of the Forming Limit Diagram of Zinc Electro-galvanized Steel Sheets
Forming limit curves (FLC) of deep drawing steel sheets have been determined experimentally and calculated on the base of the material tensile properties following the Hill, Swift, Marciniak-Kuczyński and Sing-Rao methods. Only the FLC modeled from a singly linear forming limit stress curve exhibits good consistence with experimental curve. It was established that a linearized limit stress locu...
متن کاملInfluence of the Manufacturing Process on Defects in the Galvanized Coating of High Carbon Steel Wires
This study is a detailed failure analysis of galvanized high carbon steel wires, which developed coating cracks during the torsion test performed as a quality control at the end of the manufacturing process. Careful visual inspections showed that the cracks are already present in the coating before the torsion test. In order to explain the origin of these cracks, systematic metallographic inves...
متن کاملHybrid Coatings Enriched with Tetraethoxysilane for Corrosion Mitigation of Hot-Dip Galvanized Steel in Chloride Contaminated Simulated Concrete Pore Solutions
Hybrid sol-gel coatings, named U(X):TEOS, based on ureasilicate matrices (U(X)) enriched with tetraethoxysilane (TEOS), were synthesized. The influence of TEOS addition was studied on both the structure of the hybrid sol-gel films as well as on the electrochemical properties. The effect of TEOS on the structure of the hybrid sol-gel films was investigated by solid state Nuclear Magnetic Resonan...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOP Conference Series: Materials Science and Engineering
سال: 2020
ISSN: 1757-899X
DOI: 10.1088/1757-899x/770/1/012030