Mode I Interlaminar Fracture of Glass/Epoxy Unidirectional Laminates. Part II: Numerical Analysis
نویسندگان
چکیده
منابع مشابه
Mode I Interlaminar Fracture Toughness of Natural Fiber Stitched Flax/Epoxy Composite Laminates – Experimental and Numerical Analysis
The mode I interlaminar fracture toughness of stitched and unstitched composite laminates of continuous UD flax fiber and epoxy matrix was experimentally and numerically investigated. A twistless flax fiber yarn was used for stitching purpose. The mode I interlaminar energy release rate of the unstitched and stitched laminates was experimentally determined through Double Cantilever Beam (DCB) t...
متن کاملMixed-mode I/II Interlaminar Fracture of CF/PEI Composite Material
Failures in composite materials occur mainly due to interlaminar fracture, also called delamination, between laminates. This indicates that characterizing interlaminar fracture toughness is the most effective factor in the fracture of composite materials. This study reports investigation on mixed-mode interlaminar fracture behaviour in woven carbon fibre/polyetherimide (CF/PEI) thermoplastic co...
متن کاملInterlaminar Mode II Fracture Characterization
Delamination is an important concern in the context of structural behaviour of laminated composite materials. It is known that delamination can diminish the stiffness and the strength of the material and promote structural failure. Delamination onset and growth is governed by interlaminar fracture toughness of the material. Delamination propagation is frequently dominated by mode II fracture; c...
متن کاملMode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites
1.1 This test method describes the determination of the opening Mode I interlaminar fracture toughness, GIc, of continuous fiber-reinforced composite materials using the double cantilever beam (DCB) specimen (Fig. 1). 1.2 This test method is limited to use with composites consisting of unidirectional carbon fiber and glass fiber tape laminates with brittle and tough single-phase polymer matrice...
متن کاملDeveloping a Mode Ii Fracture Model for Composite Laminates
Delamination is a critical form of failure in composite laminates which is partitioned into a combination of three pure modes namely; opening, shearing and tearing (modes I, II and III respectively). Each fracture mode contributes to the total energy required for delamination growth, due to a combination of the different damage mechanisms that occur under each mode 1-2 . To formulate reliable m...