Mode II Fatigue Delamination Growth Behaviors of Toughened Unidirectional CF/Epoxy Laminates.
نویسندگان
چکیده
منابع مشابه
Mode II delamination toughness of z-pinned laminates
Mode II delamination toughness of z-pin reinforced composite laminates is investigated using finite element (FE) method. The z-pin pullout process is simulated by the deformation and breakage of non-linear springs. A critical shear stress criterion based on linear elastic fracture mechanics is used to simulate crack growth in an end-notched-flexure (ENF) beam made of z-pinned laminates. The mod...
متن کاملA new test methodology based on structural resonance for mode I fatigue delamination growth in an unidirectional composite
A specific device has been set up to test by vibration resonance the mode I fatigue delamination growth onset of composite laminates. This test system, based on the DCB test specimen, is a mass-spring-specimen dynamic system designed to resonate. The defined operating conditions allow performing delamination propagation tests under imposed load and stopping the test under reproducible condition...
متن کاملComprehensively simulating the mixed-mode progressive delamination in composite laminates
Gao, Zhenyuan MSAA, Purdue University, May 2015. Comprehensively Simulating the Mixed-Mode Progressive Delamination in Composite Laminates. Major Professor: Wenbin Yu. Delamination, or interlaminar debonding, is a commonly observed failure mechanism in composite laminates. It is of great significance to comprehensively simulate the mixed-mode progressive delamination in composite structures bec...
متن کاملImpact Damage Detection of Toughened CFRP Laminates with Time Domain
Laminated Carbon Fiber Reinforced Polymer (CFRP) composites are very effective in weight saving in aeronautical structural components. For these laminated CFRP structures, it is, however, difficult to detect damage such as delamination, matrix cracks, and local fiber breakages caused by low velocity impact loading In the previous study in 2009, Time Domain Reflectometry (TDR) method was applied...
متن کاملExperimental study on effect of loading rate on mode I delamination of z-pin reinforced laminates
This paper presents an experimental investigation on mode I delamination of z-pinned double-cantilever-beams (DCB) and associate z-pin bridging mechanisms. Tests were performed with three types of samples: big-pin with an areal density of 2%, small-pin with an areal density of 2% and small-pin with an areal density of 0.5%. The loading rates for each type of samples were set at 1 mm/min and 100...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society for Composite Materials
سال: 1997
ISSN: 0385-2563
DOI: 10.6089/jscm.23.129