Modeling of microstructural evolution and lifetime prediction of MCrAlY coatings on nickel based superalloys during high temperature oxidation
نویسندگان
چکیده
منابع مشابه
Modeling of the microstructural evolution and lifetime prediction of MCrAlX coatings on Nickel based superalloys in high temperature oxidation
MCrAlY coatings are deposited onto superalloys to provide oxidation and corrosion protection at high temperature by the formation of a thermally grown oxide scale. In this project, the oxidation behaviour of a HVOF CoNiCrAlYSi coating on IN792 was studied for both isothermal oxidation (900, 1000 and 1100 °C) and thermal cycling (100-1100 °C). The microstructural evolution of the CoNiCrAlYSi coa...
متن کاملHigh Temperature Oxidation and Corrosion Properties of High Entropy Superalloys
The present work investigates the high temperature oxidation and corrosion behaviour of high entropy superalloys (HESA). A high content of various solutes in HESA leads to formation of complex oxides, however the Cr and Al activities of HESA are sufficient to promote protective chromia or alumina formation on the surface. By comparing the oxidation and corrosion resistances of a Ni-based supera...
متن کاملHigh Temperature Erosion- Oxidation Behavior of Nickel- Based Alloys Containing Mo in Fluidized Bed Waste Incineration
High-temperature erosion-oxidation behavior of nickel-based alloys containing 0-7 wt.% Mo in fluidized bed waste incineration conditions was studied. A stream of hot condensed air with a flow rate of 25 L/min caused hot silica sand (700 °C) mixed with 0.5 wt.% of chloride salts to hit the specimens for 250 h. By removing the erosive factor, the high-temperature oxidation behavior of the alloys ...
متن کاملEffect of Surface Morphologies on the Isothermal Oxidation Behavior of MCrAlY Coatings Fabricated by High-velocity Oxyfuel Processes
In this study, the effect of surface morphologies on the isothermal oxidation behavior of MCrAlY coatings fabricated by high-velocity oxyfuel (HVOF) processes was investigated. To do so, free standing coatings with as-sprayed and polished surfaces were isothermally oxidized at 1050°C. The thickness of the bond coat was approximately 380μm. The Ra of the as-sprayed and polished surfaces were 6.4...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Surface and Coatings Technology
سال: 2013
ISSN: 0257-8972
DOI: 10.1016/j.surfcoat.2013.05.008