Mössbauer and XRD study of hot dip galvanized alloy
نویسندگان
چکیده
منابع مشابه
Bond Strength of Hot – Dip Galvanized Reinforcement (b500b) with Concrete
P. Pokorný, D. Dobiáš, M. Vokáč – Czech Technical University – Klokner Institute, Prague, Czech Republic This paper evaluates the effect of initial corrosion damage to the surface of the hot dip galvanized steel coating in fresh concrete on its final bond strength. The tests were performed on uncoated and hot-dip galvanized ribbed reinforcements. The measurement of bond stress (τm) according to...
متن کاملDetermination of Surface Topography and Composition of Cr-Free Pretreatment Layers on Hot Dip Galvanized Steel
Topography and composition of Cr-free, titanium-based pretreatment layers on hot dip galvanized steel were studied with scanning electron microscopy, atomic force microscopy, time of flight secondary ion mass spectrometry and Auger electron spectroscopy. A layer within the target coating weight range (4-10 mg Ti/m) for industrial coil coating processes contained a micro-structure with hillocks ...
متن کاملEffect of Chemical Composition of Steel on the Structure of Hot – Dip Galvanized Coating
P. Pokorny, J. Kolisko, L. Balik – Czech Technical University – Klokner Institute, Prague, Czech Republic P. Novak – University of Chemistry and Technology, Prague, Czech Republic This article describes the effect of the content of conventional steel impurity elements on the thickness and composition of the zinc layer. This article is focused primarily on low-temperature, batch hot-dip galvaniz...
متن کاملDESCRIPTION OF STRUCTURE OF Fe-Zn INTERMETALIC COMPOUNDS PRESENT IN HOT-DIP GALVANIZED COATINGS ON STEEL
P. Pokorny, J. Kolisko, L. Balik – Czech Technical University – Klokner Institute, Prague, Czech Republic P. Novak – Institute of Chemical Technology, Prague, Czech Republic The article is describing formation, composition, morphology and crystallographic characteristics of intermetalic compounds Fe Zn present in the coating formed during the process of low-temperature hot-dip galvanizing of ca...
متن کاملDissolution-Induced Nanowire Synthesis on Hot-Dip Galvanized Surface in Supercritical Carbon Dioxide
In this study, we demonstrate a rapid treatment method for producing a needle-like nanowire structure on a hot-dip galvanized sheet at a temperature of 50 °C. The processing method involved only supercritical carbon dioxide and water to induce a reaction on the zinc surface, which resulted in growth of zinc hydroxycarbonate nanowires into flower-like shapes. This artificial patina nanostructure...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Hyperfine Interactions
سال: 2016
ISSN: 0304-3843,1572-9540
DOI: 10.1007/s10751-016-1362-x