Multiaxial fatigue behaviour of A356-T6

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Impact Properties of A356-T6 Alloys

The Charpy impact energy of A356 alloys has been measured. Instrumented Charpy impact tests have been conducted at 25, 100, 150, and 200 ~ The Charpy specimens were machined from plate castings or tapered cylindrical castings. The plates were produced in sand molds, and tapered cylinders were produced in water-cooled copper molds. Both unmodified and strontium-modified castings were tested. The...

متن کامل

Multiaxial fatigue reliability analysis of railroad wheels

A general methodology for fatigue reliability degradation of railroad wheels is proposed in this paper. Both fatigue crack initiation and crack propagation life are included in the proposed methodology using previously developed multiaxial fatigue models by the same authors. A response surface method in conjunction with design of experiments is used to develop a closed form approximation of the...

متن کامل

Fatigue Behaviour of Al 6082-T6 Friction Stir Welded Tubular Joints under Torsional Loading

The aim of the present research is to investigate the fatigue behaviour of friction stir (FS) welded tubular joints in aluminium alloy subjected to torsional fatigue loading. To manufacture the samples which were tested, an MTS I-STIR process development system was equipped with a retracting tool specifically designed for these tubular welds. Al 6082-T6 FS welded samples were tested under cycli...

متن کامل

Investigation of the T4 and T6 Heat Treatment Cycles of Semi-Solid Processed Aluminium Alloy A356

The heat treatment cycles that are currently applied to semi-solid processed components are mostly those that are in use for dendritic casting alloys. These heat treatments are not necessarily the optimum treatments. It is shown that a decrease of the solution treatment time at 540 o C from 6 hours to 1 hour does not alter the T4 or T6 tensile properties of the SSM processed A356 alloy. Slightl...

متن کامل

Porosity Control and Fatigue Behavior in A356-T61 Aluminum Alloy

Much work has been done, in recent years, to characterize the factors that cause porosity in aluminum castings, and to analyze the impact of porosity or microstructural parameters on fatigue life. What has yet to be done is systematically separate out the effects of dendrite arm spacing and largest pore size from each other, and from the underlying chemical and process parameters that influence...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Fatigue & Fracture of Engineering Materials & Structures

سال: 2012

ISSN: 8756-758X

DOI: 10.1111/j.1460-2695.2012.01702.x