Multifunctional core–shell Co–SiO2 nanowires via electrodeposition and sol–gel techniques
نویسندگان
چکیده
منابع مشابه
Molybdenum nanowires by electrodeposition.
Metallic molybdenum (Mo(o)) wires with diameters ranging from 15 nanometers to 1.0 micrometers and lengths of up to 500 micrometers (0.5 millimeters) were prepared in a two-step procedure. Molybdenum oxide wires were electrodeposited selectively at step edges and then reduced in hydrogen gas at 500 degrees C to yield Mo(o). The hemicylindrical wires prepared by this technique were self-uniform,...
متن کاملElectrodeposition of Thermoelectric Superlattice Nanowires
There is a renewed interest in the field of thermoelectrics because of the remarkable efficiency improvement that can be achieved in nanostructured materials, for example, superlattice thin films and quantum dots. Theoretical calculations predict that further enhancement of the thermoelectric figure of merit can be achieved in superlattice nanowires (zero-dimensional) [5] rather than convention...
متن کاملGrowth and Characterization of Iron Nanowires Into Anodized Aluminum Oxide Templates Using Electrodeposition Technique
The Fe nanowires were prepared by Ac electrodeposition method. The two steps anodized aluminum oxides (alumina) were used as templates for electrodeposition of magnetic nanowires. Sulfuric acid was used to anodize aluminum. The pours diameter and growth rate of alumina were investigated. The FeSO4 electrolyte was used for growth of nanowires. The prepared magnetic nanowires were characterized b...
متن کاملFabrication of cobalt-nickel binary nanowires in a highly ordered alumina template via AC electrodeposition
Cobalt-nickel (Co-Ni) binary alloy nanowires of different compositions were co-deposited in the nanopores of highly ordered anodic aluminum oxide (AAO) templates from a single sulfate bath using alternating current (AC) electrodeposition. AC electrodeposition was accomplished without modifying or removing the barrier layer. Field emission scanning electron microscope was used to study the morph...
متن کاملThe effect of pulsed electrodeposition parameters on the microstructure and magnetic properties of the CoNi nanowires
CoNi nanowires were deposited by pulsed electrodeposition technique into porous alumina templates. The effect of off time between pulses (toff) and reductive/oxidative time (treduc/oxid) on the microstructure and magnetic properties of the CoNi nanowires were investigated. Maximum coercivity and squareness were obtained for samples fabricated at treduc/oxid= 0.5 ms and toff =400 ms. The coerciv...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: RSC Advances
سال: 2015
ISSN: 2046-2069
DOI: 10.1039/c5ra13905h