Ordered mesoporous silicon carbide (OM-SiC) via polymer precursor nanocasting.
Ordered mesoporous SiC with high specific surface area (650-800 m(2) g(-1)) and well ordered pore structure was obtained via nanocasting of polycarbosilanes into SBA-15 and subsequent conversion of the polymer at 1300 degrees C.
متن کاملTuning the Pore Geometry of Ordered Mesoporous Carbons for Enhanced Adsorption of Bisphenol-A
Mesoporous carbons were synthesized via both soft and hard template methods and compared to a commercial powder activated carbon (PAC) for the adsorption ability of bisphenol-A (BPA) from an aqueous solution. The commercial PAC had a BET-surface of 1027 m²/g with fine pores of 3 nm and less. The hard templated carbon (CMK-3) material had an even higher BET-surface of 1420 m²/g with an average p...
متن کاملCharacterization of the pore structure of three-dimensionally ordered mesoporous carbons using high resolution gas sorption.
The use of colloidal crystals with various primary particle sizes as templates leads to the formation of three-dimensionally ordered mesoporous (3DOm) carbons containing spherical pores with tailorable pore size and extremely high pore volumes. We present a comprehensive structural characterization of these novel carbons by using nitrogen (77.4 K) and argon (87.3 K) adsorption coupled with the ...
متن کاملSub-150 nm mesoporous silica nanoparticles with tunable pore sizes and well-ordered mesostructure for protein encapsulation.
Despite their great potentials as biomacromolecues delivery vehicles, there are few, if any, reports on mesoporous silica nanoparticles (MSNs) simultaneously integrated with the merits of large pore size, small particle diameters and well-ordered mesostructure. Here, we designed a facile strategy for the synthesis of monodispersed MSNs using cationic surfactants (CSs) as templating agents, neut...
متن کاملpore-expanded mesoporous silica nanoparticles for PET
Larissa Miller,1 Gordon Winter,2 Benjamin Baur,2 Barbara Witulla,2 Christoph Solbach,2 Sven Reske,2,* Mika Lindén1,* 1 Department of Inorganic Chemistry II, University Ulm, Albert-Einstein-Allee 11, D-89081 Ulm, Germany 2 Clinic for Nuclear Medicine, University Ulm, Albert-Einstein-Allee 23, D-89081 Ulm, Germany Corresponding author e-mail addresses: [email protected], [email protected]
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Chemical Engineering
سال: 2014
ISSN: 1687-806X,1687-8078
DOI: 10.1155/2014/351923