New crosslinkers for electrospun chitosan fibre mats. Part II: mechanical properties
نویسندگان
چکیده
منابع مشابه
New crosslinkers for electrospun chitosan fibre mats. Part II: mechanical properties.
Few studies exist on the mechanical performance of crosslinked electrospun chitosan (CS) fibre mats. In this study, we show that the mat structure and mechanical performance depend on the different crosslinking agents genipin, epichlorohydrin (ECH), and hexamethylene-1,6-diaminocarboxysulphonate (HDACS), as well as the post-electrospinning heat and base activation treatments. The mat structure ...
متن کاملNew crosslinkers for electrospun chitosan fibre mats. I. Chemical analysis.
Chitosan (CS), the deacetylated form of chitin, the second most abundant, natural polysaccharide, is attractive for applications in the biomedical field because of its biocompatibility and resorption rates, which are higher than chitin. Crosslinking improves chemical and mechanical stability of CS. Here, we report the successful utilization of a new set of crosslinkers for electrospun CS. Genip...
متن کاملPhysical-chemical properties of cross-linked chitosan electrospun fiber mats
Chitosan fiber mats were successfully processed by electrospinning. The as-spun fiber mats were neutralized with ethanol and cross-linked with glutaraldehyde. A decrease of the fiber average diameter from 243 ± 43 nm down to 215.53 nm was observed for the neutralized and cross-linking chitosan membrane. It was found that the processing conditions do not alter the initial deacetylation degree of...
متن کاملLysozyme-loaded, electrospun chitosan-based nanofiber mats for wound healing.
In this study, a blend mixture of chitosan-ethylenediaminetetraacetic acid (CS 2 wt%-EDTA) at a weight ratio of 30/70 and polyvinyl alcohol (PVA) solution (10 wt%) was electrospun to produce fibrous mats with lysozyme (10, 20 and 30 wt%) used for wound healing. The morphology and diameter of the electrospun fiber mats with and without lysozyme were analyzed by scanning electron microscopy (SEM)...
متن کاملElectrospun chitosan-based nanofiber mats loaded with Garcinia mangostana extracts.
The aim of this study was to prepare electrospun chitosan-based nanofiber mats and to incorporate the fruit hull of Garcinia mangostana (GM) extracts into the mats. Chitosan-ethylenediaminetetraacetic acid/polyvinyl alcohol (CS-EDTA/PVA) was selected as the polymers. The GM extracts with 1, 2 and 3 wt% α-mangostin were incorporated into the CS-EDTA/PVA solution and electrospun to obtain nanofib...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of The Royal Society Interface
سال: 2013
ISSN: 1742-5689,1742-5662
DOI: 10.1098/rsif.2012.0946