New Electroless Plating Method using ZnO Thin Film as an Intermediate Layer.
نویسندگان
چکیده
منابع مشابه
Dual-Gate ZnO Thin-Film Transistors with SiNx as Dielectric Layer
We report on the fabrication of coplanar dual-gate ZnO thin-film transistors with 200-nm thickness SiNx for both top and bottom dielectrics. The ZnO film was deposited by RF magnetron sputtering on SiO2/Si substrates at 100◦C. And the thickness of ZnO film is compared with 100-nm and 40-nm. This TFT has a channel width of 100-μm and channel length of 5-μm. The fabricated coplanar dual-gate ZnO ...
متن کاملHighly Bendable In-Ga-ZnO Thin Film Transistors by Using a Thermally Stable Organic Dielectric Layer
Flexible In-Ga-ZnO (IGZO) thin film transistor (TFT) on a polyimide substrate is produced by employing a thermally stable SA7 organic material as the multi-functional barrier and dielectric layers. The IGZO channel layer was sputtered at Ar:O2 gas flow rate of 100:1 sccm and the fabricated TFT exhibited excellent transistor performances with a mobility of 15.67 cm2/Vs, a threshold voltage of 6....
متن کاملBi-layer Channel AZO/ZnO Thin Film Transistors Fabricated by Atomic Layer Deposition Technique
This letter demonstrates bi-layer channel Al-doped ZnO/ZnO thin film transistors (AZO/ZnO TFTs) via atomic layer deposition process at a relatively low temperature. The effects of annealing in oxygen atmosphere at different temperatures have also been investigated. The ALD bi-layer channel AZO/ZnO TFTs annealed in dry O2 at 300 °C exhibit a low leakage current of 2.5 × 10-13A, I on/I off ratio ...
متن کاملHigh Pressure Hydrogen Permeance of Porous Stainless Steel Coated with a Thin Palladium Film via Electroless Plating
The high-pressure (100-2500 kPa) hydrogen permeance of two membranes, each composed of a thin palladium film (~22 μm) deposited on the oxidized surface of a porous stainless steel tubular substrate (0.2 μm grade support) has been determined over the 623 – 723 K temperature range. The hydrogen flux was proportional to the H2 partial pressure in the retentate raised to an exponent of ~0.55 for on...
متن کاملElectroless Nickel Plating with Hypophosphite
In the previous chapter, the components of electroless nickel plating baths were discussed from the viewpoint of the function each performs in the bath, with little attention paid to their effect on the plating process. The metal and the electron source (the reducing agent) are consumed in the electroless plating reaction and so their concentrations in the bath are continuously decreasing. Ther...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 1994
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.45.498