NUMERICAL INVESTIGATION OF CRACK ORIENTATION IN THE FRETTING FATIGUE OF A FLAT ROUNDED CONTACT
The growth of slant cracks by fretting fatigue of a half plane in contact with a flat rounded pad was studied. The mode I and mode II stress intensity factors for cracks of various lengths and directions were calculated using the semi-analytical method of the distribution of dislocations, and their cumulative effect on the crack growth was investigated using the strain energy density criterion....
متن کاملNumerical Modeling of Fretting Wear
In this paper, a review of some techniques proposed in the literature for modelling fretting wear is presented. Fretting wear occurs when surfaces are degraded and materials are removed due to a small relative oscillatory motion between two contact surfaces. Due to the continuous change in the shape of a structure during its lifetime, the design of engineering components subjected to fretting w...
متن کاملNumerical Study of the Effects of Residual Stress on Fretting Fatigue Using XFEM
Residual compressive stress can improve fretting fatigue strength. In this paper, the effects of residual stress on fretting fatigue of Al 2024-T351 alloy specimens are studied using a numerical approach. The extended finite element method combined with the cyclic cohesive zone model is adopted to model fretting fatigue crack growth behavior. It is shown that residual stress changes the frettin...
متن کاملOn the Convergence of Stresses in Fretting Fatigue
Fretting is a phenomenon that occurs at the contacts of surfaces that are subjected to oscillatory relative movement of small amplitudes. Depending on service conditions, fretting may significantly reduce the service life of a component due to fretting fatigue. In this regard, the analysis of stresses at contact is of great importance for predicting the lifetime of components. However, due to t...
متن کاملFretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy
An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scann...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2011
ISSN: 1742-6596
DOI: 10.1088/1742-6596/305/1/012061