Optimal Chemical Composition in Fe-Cr-Ni Alloys for Ultra Grain Refining by Reversion from Deformation Induced Martensite.
نویسندگان
چکیده
منابع مشابه
Microstructural Examination of Ni-ion Irradiated Fe-Ni-Cr Alloys Followed to Micro-zone Deformation
Examination of deformation microstructures induced by micro-indentation technique by means of transmission electron microscopy following an MV range metallic ion irradiation was performed in order to study the influence of irradiation-produced microstructural defects on plastic deformation behavior of materials. In this work, specimens of an Fe-Cr-Ni austenitic model ternary alloy before and af...
متن کاملLimit of Dislocation Density and Ultra-Grain-Refining on Severe Deformation in Iron
It is well-known that severe deformation to metals causes a direct grain refinement of the matrix without special heat-treatments due to the mechanism of dynamic continuous recrystallization (DCR). However, the microstructural revolution during severe deformation is seemed to be different depending on the deformation mode, namely the direction of deformation. In general, multi-directional defor...
متن کاملThermally activated growth of lath martensite in Fe–Cr–Ni–Al stainless steel
The austenite-to-martensite transformation in a partially hardened stainless steel containing 17wt %Cr, 7wt %Ni and 1wt % Al was investigated with Vibrating Sample Magnetometry and Electron Back-Scatter Diffraction. Magnetometry demonstrated that measurable martensite formation can be suppressed on fast cooling to 77K as well as on subsequent fast heating to 373 K. Surprisingly, martensite form...
متن کاملThermally activated growth of lath martensite in Fe- Cr-Ni-Al precipitation hardenable stainless steel
The austenite-to-martensite transformation in a partially hardened stainless steel containing 17wt %Cr, 7wt %Ni and 1wt % Al was investigated with Vibrating Sample Magnetometry and Electron Back-Scatter Diffraction. Magnetometry demonstrated that measurable martensite formation can be suppressed on fast cooling to 77K as well as on subsequent fast heating to 373 K. Surprisingly, martensite form...
متن کاملPhase transitions in nanostructured Fe–Cr–Ni alloys prepared by mechanical alloying
Phase transition of Fe–18Cr–8Ni, Fe–15Cr–15Ni and Fe–15Cr–25Ni alloys during mechanical alloying (MA) and after subsequent annealing as studied. For Fe–18Cr–8Ni and Fe–15Cr–15Ni the resulting structure by MA was a nanostructured single-phase BCC solid solution ( ) which iffers from that predicted from equilibrium phase diagram. Furthermore, the equilibrium structure was not achieved after heat ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ISIJ International
سال: 1991
ISSN: 0915-1559
DOI: 10.2355/isijinternational.31.721