Oxygen Reduction, Transport and Separation in Low Silver Content Scandia-Stabilized Zirconia Composites
نویسندگان
چکیده
منابع مشابه
Oxygen reduction via grain boundary transport in thin film platinum electrodes on yttria stabilized zirconia
Model-type sputter deposited platinum microelectrodes with different grain sizes were investigated on single crystalline yttria stabilized zirconia (YSZ) by means of impedance spectroscopy. Measurements on single platinum microelectrodes could be continuously performed for > 100 h and from 250 to 800 °C without losing contact. From the temperature dependence, two parallel reaction pathways for ...
متن کاملLow-Temperature Superionic Conductivity in Strained Yttria-Stabilized Zirconia
We report very high lateral ionic conductivities in epitaxial cubic yttria-stabilized zirconia synthesized on single crystal SrTiO3 and MgO substrates by reactive direct current magnetron sputtering. Superionic conductivities (i.e., ionic conductivities of the order ~1 Ω -1 cm -1 ) are observed at 500 oC for 58-nm-thick films on MgO. Our results indicate a superposition of two parallel contribu...
متن کاملElaboration of Alumina-Zirconia Composites: Role of the Zirconia Content on the Microstructure and Mechanical Properties
Alumina-zirconia (AZ) composites are attractive structural materials, which combine the high hardness and Young's modulus of the alumina matrix with additional toughening effects, due to the zirconia dispersion. In this study, AZ composites containing different amounts of zirconia (in the range 5-20 vol %) were prepared by a wet chemical method, consisting on the surface coating of alumina powd...
متن کاملOxygen Transport and Association in Yttria Stabilised Zirconia
1. Introduction 1. Introduction Zirconia is widely used due to its high oxygen diffusivity in various technological applications like gas sensors, fuel cells, catalytic membranes etc. The material shows an excellent thermal stability, combined with very good mechanical properties.
متن کاملGrain size influence on the thermal properties of stabilized zirconia-nano spinel (Al2O3-MgO) composites
Abstract. Cubic crystalline oxides such as Y2O3 and MgO is used to stabalized zirconia phases at high temperature. In this paper the Y2O3 powder was added to stabilized zirconia and preparing a mixture of MgAl2O4 Spinel by mixing 1mol of nano-MgO with 1 mol of nano-Al2O3 powders. The spinel was added to the Y2O3-ZrO2 by various weight percentage (5, 10, 15, 20 and 25 wt%), and after that the sp...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of The Electrochemical Society
سال: 2017
ISSN: 0013-4651,1945-7111
DOI: 10.1149/2.0081710jes