Performance of Cr-doped vanadia/titania catalysts for low-temperature selective catalytic reduction of NOx with NH3
نویسندگان
چکیده
منابع مشابه
Low temperature selective catalytic reduction of NOx with NH3 over Mn-based catalyst: A review
The removals of NOx by catalytic technology at low temperatures (100–300 °C) for industrial flue gas treatment have received increasing attention. However, the development of low temperature catalysts for selective catalytic reduction (SCR) of NOx with ammonia is still a challenge especially in the presence of SO2. The current status of using Mn-based catalysts for low temperature SCR of NOx wi...
متن کاملIron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3.
The catalysts of iron-doped Mn-Ce/TiO2 (Fe-Mn-Ce/TiO2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction (SCR) of NO with NH3. It was found that the NO conversion over Fe-Mn-Ce/TiO2 was obviously improved after iron doping compared with that over Mn-Ce/TiO2. Fe-Mn-Ce/TiO2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity. The results...
متن کاملThe Selective Catalytic Reduction of NOx with NH3 over Titania Supported Rhenium Oxide Catalysts
Titania supported vanadium oxide catalysts have been demonstrated to be very efficient catalysts for the selective reduction of NOx with NH3 and have found widespread industrial application for the control of NOx emissions from stationary sources (1). Characterization studies have demonstrated that supported vanadium oxide catalysts consist of a two-dimensional metal oxide overlayer on the oxid...
متن کاملPromotional effect of Si-doped V2O5/TiO2 for selective catalytic reduction of NOx by NH3.
TiO2 supports doped with different amounts of Si were prepared by a sol-gel method, and 1 wt% vanadia (V2O5) loaded on Si-doped TiO2 was obtained by an impregnation method. The mole ratio of Si/Ti was 0.2, NOx conversion exceeds 94% at 300 degrees C and GHSV of 41,324 hr(-1), which is about 20% higher than pure V2O5/TiO2. The catalysts were characterized by XRD, BET, TEM, FT-IR, NH3-TPD, XPS, H...
متن کاملLow Temperature Performance of Selective Catalytic Reduction of NO with NH3 under a Concentrated CO2 Atmosphere
Selective catalytic reduction of NOx with NH3 (NH3-SCR) has been widely investigated to reduce NOx emissions from combustion processes, which cause environmental challenges. However, most of the current work on NOx reduction has focused on using feed gas without CO2 or containing small amounts of CO2. In the future, oxy-fuel combustion will play an important role for power generation, and this ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chinese Journal of Catalysis
سال: 2015
ISSN: 1872-2067
DOI: 10.1016/s1872-2067(15)60884-1