pH-sensitive polyvinylpyrrolidone-acrylic acid hydrogels: Impact of material parameters on swelling and drug release
نویسندگان
چکیده
منابع مشابه
pH Sensitive Hydrogel Based Acrylic Acid for Controlled Drug Release
Hydrogels, due to their unique potentials such as high-water content and hydrophilicity are interest for the controlled release of drug molecules. The present study aims to create a controlled-release system through the preparation and characterization of hydrogels based on pH-sensitive polymers such as poly (acrylic acid). Poly (acrylic acid), p(AA), hydrogel has been synthesized by radical po...
متن کاملStructural Parameters and Swelling Behavior of pH Sensitive Poly(acrylamide-co-acrylic acid) Hydrogels
In the present work, hydrogels based on acrylamide (AAm) and acrylic acid (AAc), crosslinked with N,N’-methylenebisacrylamide (MBAAm) were prepared by free radical polymerization in solution. The effect of initial AAm/AAc mole ratio and nominal crosslinking ratio (moles of crosslinking agent/moles of polymer repeat unit) on the dynamic and equilibrium swelling behaviour of hydrogels was investi...
متن کاملSynthesis of pH Sensitive Hydrogels Based on Poly Vinyl Alcohol and Poly Acrylic Acid
In this research, hydrogels based on poly vinyl alcohol and poly acrylic acid blend were prepared which were cross-linked by applied thermal conditions. Afterward, effects of time and heating on water uptake were investigated. The highest water uptake value exhibited by the sample that was heated for 20 min. at 110 ºC was about 2129% after 4 days at equilibrium state. Hydrogels exhibited p...
متن کاملph sensitive hydrogel based acrylic acid for controlled drug release
hydrogels, due to their unique potentials such as high-water content and hydrophilicity are interest for the controlled release of drug molecules. the present study aims to create a controlled-release system through the preparation and characterization of hydrogels based on ph-sensitive polymers such as poly (acrylic acid). poly (acrylic acid), p(aa), hydrogel has been synthesized by radical po...
متن کاملSynthesis and Swelling Behavior of pH-Sensitive Semi-IPN Superabsorbent Hydrogels Based on Poly(acrylic acid) Reinforced with Cellulose Nanocrystals
pH-sensitive poly(acrylic acid) (PAA) hydrogel reinforced with cellulose nanocrystals (CNC) was prepared. Acrylic acid (AA) was subjected to chemical cross-linking using the cross-linking agent MBA (N,N-methylenebisacrylamide) with CNC entrapped in the PAA matrix. The quantity of CNC was varied between 0, 5, 10, 15, 20, and 25 wt %. X-ray diffraction (XRD) data showed an increase in crystallini...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Brazilian Journal of Pharmaceutical Sciences
سال: 2014
ISSN: 1984-8250
DOI: 10.1590/s1984-82502011000100018