Phase Transformations and Fatigue of NiTi
نویسندگان
چکیده
منابع مشابه
Phase Transformations in NiTi Endodontic Files and Fatigue Resistance
NiTi endodontic files allow for clinical enlargement of harshly curved root canals. However, files rotated under severe flexion might fracture unexpectedly, remain inside teeth and thus, hinder treatment outcome. ProFile .06(35) are among the most commonly used rotary files. In the present study, 10 of these brand new instruments were used to perform DSC on their cutting regions and determine t...
متن کاملCrystallography of the B 2 → R → B 19 ′ phase transformations in NiTi
The crystallography of B2 to R-phase and the subsequent R-phase to B19′ martensite transitions was analysed in NiTi alloys. Using the energy minimization theory of martensitic transformations, the habit plane and twin plane normals were established for the R-phase, B19′ martensite variants as a function of rhombohedral angle . Two types of twins, classified as {1 0 0}〈0 1 1〉 and {1 1 0}〈0 0 1〉 ...
متن کاملFatigue crack-growth in shape-memory NiTi and NiTi–TiC composites
An experimental study was conducted to examine the room-temperature fatigue crack-growth characteristics of shape-memory NiTi matrix composites reinforced with 10 and 20 vol.% of TiC particles. Microstructural characterization of these hot-isostatically-pressed materials shows that the TiC particles do not react with the NiTi matrix and that they lack any texture. Overall fatigue crack-growth c...
متن کاملStress-induced martensitic transformations in NiTi and NiTi–TiC composites investigated by neutron diffraction
Superelastic NiTi (51.0 at.% Ni) specimens reinforced with 0, 10 and 20 vol.% TiC particles were deformed under uniaxial compression while neutron diffraction spectra were collected. The experiments yielded in-situ measurements of the thermoelastic stress-induced transformation. The evolution of austenite/martensite phase fractions and of elastic strains in the reinforcing TiC particles and the...
متن کاملPhase transformation and deformation behavior of NiTi-Nb eutectic joined NiTi wires
NiTi wires were brazed together via eutectic reaction between NiTi and Nb powder deposited at the wire contact region. Phase transformation and deformation behavior of the NiTi-Nb eutectic microstructure were investigated using transmission electron microscopy (TEM) and cyclic loading-unloading tests. Results show that R phase and B19' martensite transformation are induced by plastic deformatio...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATEC Web of Conferences
سال: 2015
ISSN: 2261-236X
DOI: 10.1051/matecconf/20153303011