Phase Transformations in Cu-Zr Multilayers

Phase Separation and Crystallization in Cu-Zr Metallic Glasses

The structural behavior of rapidly quenched Cu-Zr amorphous alloys was analyzed. High energy X-ray diffraction patterns and atomic pair correlation functions exhibit monotonic changes with composition. The experimental results can be well described by a solid solution-like replacement of Cu and Zr atoms in the whole composition range. No indications are observed that would support the existence...

Formation of Amorphous Phase in the Binary Cu-Zr Alloy System

The aim of this work is to elucidate the formation of the amorphous phase in the Cu-Zr binary alloy system. It was found that 1 mm diameter rods with a fully amorphous structure can be prepared in a relatively wide range of compositions. In contrast, the formation of 2 mm diameter rods was achieved only for the Cu64Zr36 alloy and in the range of Cu53Zr47 Cu50Zr50, which are compositions near th...

Plastic Deformation Modes of CuZr/Cu Multilayers.

We synthesized CuZr/Cu multilayers and performed nanoindentation testing to explore the dependence of plastic deformation modes on the thickness of CuZr layers. The Cu layers were 18 nm thick and the CuZr layers varied in thickness from 4 nm to 100 nm. We observed continuous plastic co-deformation in the 4 nm and 10 nm CuZr - 18 nm Cu multilayers and plastic-induced shear instability in thick C...

Josephson properties of Nb/Cu multilayers.

Supercooled melting in multicomponent Zr–Al–Cu–Ni diffusion couples

Diffusion couples combining a hcp Zr90Al10 supersaturated solid solution with a fcc Cu64Ni36 solid solution were annealed at 410 °C for different times. The reaction at the interface was investigated by transmission electron microscopy and energy dispersive x-ray spectroscopy. The investigations show the formation of a noncrystalline layer at the interface between the two solid solutions that g...