Phases changes of the AK12MMgN-18%SiCp composite alloy after severe plastic deformation and annealing
نویسندگان
چکیده
منابع مشابه
Superplasticity of a fine-grained Mg–1.5 wt% Gd alloy after severe plastic deformation
The strain rate sensitivity (SRS) of Mg–1.5 wt% Gd processed by conventional extrusion and 2 passes of simple shear extrusion (SSE) was investigated by shear punch testing. Shear punch tests were conducted at initial shear strain rates in the range of 0.003–0.3 s-1 and at temperatures in the range of 573–773 K. A fine-grained microstructure with an average grain size of about 2.5 µm, obtained a...
متن کاملPLASTIC DEFORMATION BEHAVIOUR AT THE WORN SURFACE OF NOVEL CAST AL-ALLOY-TICP COMPOSITE
An AI-7wt%Si-5vol%TiCp was worn against a cast iron disc in a tri-pin-on-disc machine, under dry sliding conditions at the sliding speed of 0.24 m/s and applied loads of 6, 20 and 40 N/pin. Stress-strain (`3-^9) curves were constructed by measuring the microhardness and the equivalent strain gradients in near surface regions on the cross-sectional surface prepared parallel to sliding direction....
متن کاملEBSD characterization of nano/ultrafine structured Al/Brass composite produced by severe plastic deformation
In the present work, nano/ultrafine structured Al/Brass composite was produced by accumulative roll bonding (ARB) up to eight cycles. The evolution of grain refinement and deformation texture and their effect on the mechanical properties were investigated. It was observed that by increasing the ARB cycles, due to the difference in flow properties of the metal constituents, brass layers necked, ...
متن کاملTHE EFFECT OF SEVERE PLASTIC DEFORMATION ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AS-CAST AZ31
The evolution of microstructure and mechanical properties of a magnesium cast alloy (AZ31) processed by equal channel angular pressing (ECAP) at two different temperatures were investigated. The as-cast alloy with an average grain size of 360 was significantly refined to about 5 after four ECAP passes at 543 K. Grain refinement was achieved through dynamic recrystallization (DRX) du...
متن کاملNumerical Analysis of Severe Plastic Deformation by High Pressure Torsion
High-pressure torsion (HPT) is a metal processing method in which the sample is subjected to a very high plastic shear deformation. This process can produce exceptional levels of grain refinement, and provides a corresponding improvement in mechanical properties. To investigate the stress and strain distribution due to HPT process finite element simulation were conducted to investigate effectiv...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Letters on Materials
سال: 2017
ISSN: 2218-5046,2410-3535
DOI: 10.22226/2410-3535-2017-1-3-7