Plasma Nitriding of Steel Heated by External Electric Heater.
نویسندگان
چکیده
منابع مشابه
Nanosized precipitates in H13 tool steel low temperature plasma nitriding
A comprehensive study of pulsed nitriding in AISI H13 tool steel at low temperature (400°C) is reported for several durations. X-ray diffraction results reveal that a nitrogen enriched compound (-Fe2-3N, iron nitride) builds up on the surface within the first process hour despite the low process temperature. Beneath the surface, X-ray Wavelength Dispersive Spectroscopy (WDS) in a Scanning Elec...
متن کاملSurface Modification of Titanium by Plasma Nitriding
A systematic investigation was undertaken on commercially pure titanium submitted to plasma nitriding. Thirteen different sets of operational parameters (nitriding time, sample temperature and plasma atmosphere) were used. Surface analyses were performed using X-ray diffraction, nuclear reaction and scanning electron microscopy. Wear tests were done with stainless steel Gracey scaler, sonic app...
متن کاملCOMPARISON OF PROPERTIES OF TiN/TiCN AND PLASMA NITRIDING/TiCN FILMS DEPOSITED ON THE TOOL STEEL BY PULSED DC- PACVD
In this work, TiN/TiCN & PN/TiCN multilayer films were deposited by plasma- assisted chemical vapour deposition (PACVD). Plasma nitriding (PN) and TiN intermediate layer prior to coating leads to appropriate hardness gradient and it can greatly improve the mechanical properties of the coating. The composition, crystalline structure and phase of the films were investigated by X-ray d...
متن کاملDuplex Surface Treatment of AISI 1045 Steel via Plasma Nitriding of Titanized Layer
In this Study, surface of medium carbon steel (AISI 1045) was modified by titanizing followed by plasma nitriding. Titanizing was performed using pack cementation method, in a pack mixture of ferrotitanium, ammonium chloride and alumina, at 1223 K for 45 and 180 min. Plasma-nitriding was conducted at two temperatures of 803 and 823 K for 5 h, in a gas mixture of 75%N2+25%H2. The samples were c...
متن کاملSome Consideration on Double Layer Structure in Plasma Assisted Nitriding of Austenitic Stainless Steel
Low temperature plasma assisted nit riding treatments of 316 stainless steel produce a complex layer constituted by tow different metastable f.c.c. solid solution denoted ( γ N1 and γ N2 ). About the formation of these double layers, different hypothesis was proposed in the literature. For verifying these hypotheses, the effects of differentes conditions such as nit riding temperature, cleaning...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 2002
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.53.550