Polymorphic Transformations of Tricalcium Silicate
نویسندگان
چکیده
منابع مشابه
Properties of Tricalcium Silicate Sealers.
INTRODUCTION Sealers based on tricalcium silicate cement aim at an interaction of the sealer with the root canal wall, alkalinity with potential antimicrobial activity, and the ability to set in a wet field. The aim of this study was to characterize and investigate the properties of a new tricalcium silicate-based sealer and verify its compliance to ISO 6876 (2012). METHODS A new tricalcium s...
متن کاملUnderstanding silicate hydration from quantitative analyses of hydrating tricalcium silicates
Silicate hydration is prevalent in natural and technological processes, such as, mineral weathering, glass alteration, zeolite syntheses and cement hydration. Tricalcium silicate (Ca3SiO5), the main constituent of Portland cement, is amongst the most reactive silicates in water. Despite its widespread industrial use, the reaction of Ca3SiO5 with water to form calcium-silicate-hydrates (C-S-H) s...
متن کاملHydration of tricalcium silicate in the presence of synthetic calcium–silicate–hydrate
The early age-hydration of tricalcium silicate, the main chemical compound in Portland cement, was studied in the presence of synthetic calcium silicate hydrate (C–S–H) addition having C/S ratios 1⁄4 0.8 and 1.2. Isothermal conduction calorimetry, scanning electron microscopy, differential scanning calorimetry and Si MAS NMR were employed in order to investigate events occurring during various ...
متن کاملCytotoxicity and physical properties of tricalcium silicate-based endodontic materials
OBJECTIVES The aim of this study was to evaluate the cytotoxicity, setting time and compressive strength of MTA and two novel tricalcium silicate-based endodontic materials, Bioaggregate (BA) and Biodentine (BD). MATERIALS AND METHODS Cytotoxicity was evaluated by using a 2,3-bis(2-methoxy-4-nitro-5-sulfophenyl)-5-((phenylamino)carbonyl)-2H-tetrazolium hydroxide (XTT) assay. Measurements of 9...
متن کاملThe rhombohedral structure of tricalcium silicate at 1200°C
Crystals of tricalcium silicate having a monoclinic superstructure transformed into a rhombohedral structure when they were heated at 1200 °C with gas flame: a=7.135(6) A, c=25.586(15) A, space group R3m, and contents of 9 x Ca2,9sSio,9sAlo,o40s. The rhombohedral structure has been determined based on a set of 371 diffraction intensities measured with a single-crystal diffractometer giving a fi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Association, Japan
سال: 1971
ISSN: 0009-0255,1884-2127
DOI: 10.2109/jcersj1950.79.910_183