Porous Titanium for Biomedical Applications: Evaluation of the Conventional Powder Metallurgy Frontier and Space-Holder Technique
نویسندگان
چکیده
منابع مشابه
Porous Titanium Scaffolds Produced by Powder Metallurgy for Biomedical Applications
Department of Bioscience and Buccal Diagnosis, São Jose dos Campos School of Dentistry, State University of São Paulo – UNESP, Av. Engenheiro Francisco José Longo, 777, 12245-000 São José dos Campos SP, Brazil National Institute of Technology, Av. Venezuela, 200, Centro, Rio de Janeiro RJ, Brazil Department of Materials, Air and Space Institute, CTA, Praça Mal. do Ar Eduardo Gomes, 14, 12904-00...
متن کاملStiffness variation of porous titanium developed using space holder method
The excellent properties of Ti have resulted in its generalised use for bone implants. However, Ti is very stiff in comparison with human cortical bone, and this creates problems of bone weakening and loosening of the implant. This article discusses the mechanical properties (flexural and compressive strength, and stiffness) of porous Ti–6Al–4V specimens developed using the space holder method....
متن کاملPorous, Superelastic NiTi Produced by Powder-Metallurgy
Near-stoichiometric NiTi was foamed in the solid state at elevated temperatures through creep expansion of highpressure argon pores previously entrapped during powder consolidation. A sample with 17% porosity was found to be superelastic up to a compressive stress of 800 MPa.
متن کاملTitanium nanostructures for biomedical applications.
Titanium and titanium alloys exhibit a unique combination of strength and biocompatibility, which enables their use in medical applications and accounts for their extensive use as implant materials in the last 50 years. Currently, a large amount of research is being carried out in order to determine the optimal surface topography for use in bioapplications, and thus the emphasis is on nanotechn...
متن کاملAnalysis of bending strength of porous titanium processed by space holder method
Porous titanium specimens have been produced by means of the space holder method. Titanium grade 3 (TiCP3) has been used as material and ammonium bicarbonate as spacer. Process parameters (compaction pressure, metal grain size range and spacer volume) influence on porosity morphology and distribution and bending strength has been analysed. The results denote an important loss of strength when c...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Sciences
سال: 2019
ISSN: 2076-3417
DOI: 10.3390/app9050982