POROUS TITANIUM PHOSPHATE GLASS-CERAMICS WITH BACTERIOSTATIC ACTIVITIES
نویسندگان
چکیده
منابع مشابه
Iron Phosphate Glass-ceramics
The crystallization of 40Fe2O3-60P2O5, 10ZnO-30Fe2O3-60P2O5 and (43.3−x)PbO–(13.7+x)Fe2O3–43P2O5, (0 < x < 30), glasses and glassceramic have been investigated. The structural evolution of glasses during heat treatment at various temperatures and the tendency for crystallization for series of glasses with modified composition are characterized by a dendrite-like phase separation in the early st...
متن کاملDetermination of the Nucleation and Crystallization Parameters for Making Nanoporous Titanium Phosphate Glass-ceramics
Nanoporous glass-ceramics were prepared with composition 45CaO-25TiO2-35P2O5 (mol%). Two molar percent of Na2O was added as a flux to the composition. With the aforementioned composition, glass melted and crystallized into glass-ceramics containing β-Ca3(PO4)2 and CaTi4(PO4)6 as the main phases. The differential thermal analysis (DTA) was conducted to determine the suitable temperatures f...
متن کاملAddition of Alumina to Nanoporous Calcium Titanium Phosphate Glass-Ceramics and its Effects on Crystallization Behavior
Microporous Calcium Titanium Phosphate glass-ceramics have many uses in high-tech industries. For example, they have applications in catalysts industry. In this study, different molar percentages of alumina were added to a glass with P2O5 30, CaO 45, TiO2 25 (mol%) composition. The samples were melted at 1350°C and crystallization heat treatment was performed on...
متن کاملTitanium phosphate glass microspheres for bone tissue engineering.
We have demonstrated the successful production of titanium phosphate glass microspheres in the size range of ∼10-200 μm using an inexpensive, efficient, easily scalable process and assessed their use in bone tissue engineering applications. Glasses of the following compositions were prepared by melt-quench techniques: 0.5P₂O₅-0.4CaO-(0.1-x)Na₂O-xTiO₂, where x=0.03, 0.05 and 0.07 mol fraction (d...
متن کاملPhosphate Glass Porous Microspheres for Bone Tissue Regeneration Applications
The interest in use of Calcium phosphate (CaP) based glasses as resorbable implantable devices has been steadily increasing due to their unique properties, such as their chemical compositions which can resemble the mineral content of natural bone, controllable degradation profiles coupled with controlled ion release rates and their cytocompatibility [1]. This work focussed on developing both bu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Phosphorus Research Bulletin
سال: 1996
ISSN: 0918-4783
DOI: 10.3363/prb1992.6.0_253